Dispercoll® U XP 2643
Anionic polyurethane dispersion for the formulation of adhesives e.g. for packaging, automotive, footwear and construction industries. Suitable for bonding at RT and low bondline temperatures.
i
Market Switch
Selection will influence the results you get.
About
Product Types
- Dispersion
- Waterbased dispersion
- PU dispersion - high molecular
- PU dispersion
Material
- Adhesives
- Moisture resistant, Fast bonding, Waterborne, Heat resistant, Heat activated, Contact adhesive
General Characterization
Aqueous polyurethane dispersion.
Dispercoll® U XP 2643 is an aqueous dispersion of an anionic modified polyurethane. It is a raw material for the formulation of adhesives for use in, for example, the packing, automotive, footwear and construction industries. Because of the characteristic polymer properties Dispercoll® U XP 2643 is suitable for bondings at roomtemperature and applications at low heat activation temperatures.
Dispercoll® U XP 2643 is an aqueous dispersion of an anionic modified polyurethane. It is a raw material for the formulation of adhesives for use in, for example, the packing, automotive, footwear and construction industries. Because of the characteristic polymer properties Dispercoll® U XP 2643 is suitable for bondings at roomtemperature and applications at low heat activation temperatures.
Storage Conditions
- Storage in original sealed Covestro container.
- Recommended storage temperature: 10 - 23 °C.
- Protect from direct sunlight, frost, heat and foreign material.
General information: The product is sensitive to cold temperatures below +10 °C. Freezing can damage the product irreversibly. Temperatures higher than 30 °C should be avoided. Prolonged storage at higher temperatures may affect the product properties. Containers must be kept sealed and protected from direct sunlight as otherwise the evaporation of water will result in the formation of a non-redispersible polymer film. After extended storage time sedimentation can occur. The material can be proceeds without quality losses after homogenization.
- Recommended storage temperature: 10 - 23 °C.
- Protect from direct sunlight, frost, heat and foreign material.
General information: The product is sensitive to cold temperatures below +10 °C. Freezing can damage the product irreversibly. Temperatures higher than 30 °C should be avoided. Prolonged storage at higher temperatures may affect the product properties. Containers must be kept sealed and protected from direct sunlight as otherwise the evaporation of water will result in the formation of a non-redispersible polymer film. After extended storage time sedimentation can occur. The material can be proceeds without quality losses after homogenization.
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Characteristics
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Minimum film-forming temperature | DIN ISO 2115 | °C | approx. 5 |
| Density | DIN 51 757 | g/cm3 | approx. 1.1 |
Specifications
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Non-volatile content (1g / 1h / 125 °C) | DIN EN ISO 3251 | % | 39 - 41 |
| pH-value | DIN ISO 976 | 6.0 - 9.0 | |
| Viscosity at 23 °C,spindle L 2 / 30 rpm | DIN EN ISO 2555 | mPa*s | < 1,000 |