Baybond® PU 417
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
Anionic/non-ionic polyester urethane polymer based on aliphatic isocyanates.
As the film-forming component in glass fiber sizes.
As the film-forming component in glass fiber sizes.
Storage Conditions
- Storage in original sealed Covestro container.
- Recommended storage temperature: 5 - 30 °C.
- Protect from frost, heat and foreign material.
General information: Before use the product must be homogenized by stirring. The product can not be used if it has been frozen. The containers must be well closed to prevent the evaporation of water which may result in the formation of non-redispersible film.
- Recommended storage temperature: 5 - 30 °C.
- Protect from frost, heat and foreign material.
General information: Before use the product must be homogenized by stirring. The product can not be used if it has been frozen. The containers must be well closed to prevent the evaporation of water which may result in the formation of non-redispersible film.
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Characteristics
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Density at 23 °C | DIN EN ISO 2811/1 | g/ml | ca. 1.1 |
Specifications
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| pH at 23 °C (supply form) | M022-ISO 976 | 7.0 - 10 | |
| Non-volatile content (0.9 - 1.1g/1h/125°C,convection oven) | M020-ISO 3251 | % | 49 - 51 |
| Viscosity at 23°C spindle L2/30 rpm | M092-ISO 2555 | mPa*s | < 1000 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com