Makrolon® DQ5942 FR
MVR (300 °C/1.2 kg) 5.0 cm³/10 min; light diffusion grade; medium diffusion; UV stabilized; flame retardant
i
Market Switch
Selection will influence the results you get.
About
Product Types
- Polycarbonate
Material
- Plastics
- Transparent, UV stable, Optical quality, Flame retardant
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Barrel Temperatures - Front | - | °C | 280 - 290 | |
Barrel Temperatures - Middle | - | °C | 270 - 280 | |
Barrel Temperatures - Nozzle | - | °C | 290 - 300 | |
Barrel Temperatures - Rear | - | °C | 250 - 260 | |
Dry Air Drying Temperature | - | °C | 120 | |
Dry Air Drying Time | - | h | 2 - 3 | |
Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
Melt temperatures | - | °C | 280 - 320 | |
Moisture Content max. (%) | - | % | <= 0.02 | |
Mold Temperatures | - | °C | 80 - 120 | |
Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
Shot-to-Cylinder Size | - | % | 30 - 70 | |
Standard Melt temperature | - | °C | 300 | |
Vent Depth | - | mm | 0.025 - 0.075 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Burning behavior UL 94 [UL recognition] | UL 94 | 0.8 mm | Class | V-0 |
Burning behavior UL 94-5V [UL recognition] | UL 94 | 3.0 mm | Class | 5VA |
Glow wire test (GWFI) | IEC 60695-2-12 | 0.75 mm | °C | 960 |
Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 960 |
Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 960 |
Glow wire test (GWIT) | IEC 60695-2-13 | 0.75 mm | °C | 850 |
Glow wire test (GWIT) | IEC 60695-2-13 | 1.5 mm | °C | 850 |
Glow wire test (GWIT) | IEC 60695-2-13 | 3.0 mm | °C | 850 |
Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 135 |
Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 120 |
Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 141 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Charpy impact strength | ISO 179/1eU | -30 °C | kJ/m² | N |
Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 7C |
Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | 44 |
Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 73 |
Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 53 |
Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2300 |
Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6 |
Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 66 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Half power angle | Covestro Test | 1 mm | ° | 25 |
Half power angle | Covestro Test | 2 mm | ° | 42 |
Half power angle | Covestro Test | 3 mm | ° | 50 |
Half power angle | Covestro Test | 4 mm | ° | 53 |
Luminous transmittance | ISO 13468-2 | 1 mm | % | 79 |
Luminous transmittance | ISO 13468-2 | 2 mm | % | 63 |
Luminous transmittance | ISO 13468-2 | 3 mm | % | 53 |
Luminous transmittance | ISO 13468-2 | 4 mm | % | 46 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 260 °C | Pa*s | 500 |
Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C | Pa*s | 230 |
Melt viscosity | b.o. ISO 11443-A | 50 s^-1^/ 260 °C | Pa*s | 1840 |
Melt viscosity | b.o. ISO 11443-A | 50 s^-1^/ 300 °C | Pa*s | 640 |
Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 5 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
Injection molding - Melt temperature | ISO 294 | °C | 290 | |
Injection molding - Mold temperature | ISO 294 | °C | 80 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Density | ISO 1183-1 | kg/m³ | 1190 |