Makrolon® GF9002

MVR (300 °C/1.2 kg) 15 cm³/10 min; 10 % glass fiber reinforced; flame retardant; UL 94V-0/1.2 mm; low viscosity; easy release; electrical/electronic; housing parts with low wall thickness

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • Polycarbonate

Material

Plastics
Dimensionally stable, Flame retardant

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 280 - 290
Barrel Temperatures - Middle - °C 270 - 280
Barrel Temperatures - Nozzle - °C 290 - 300
Barrel Temperatures - Rear - °C 250 - 260
Dry Air Drying Temperature - °C 120
Dry Air Drying Time - h 2 - 3
Hold Pressure (% of injection pressure) - % 50 - 75
Melt temperatures - °C 280 - 320
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 80 - 120
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt temperature - °C 300
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 [UL recognition] UL 94 1.2 mm Class V-0
Burning behavior UL 94 [UL recognition] UL 94 0.75 mm Class V-1
Burning rate (US-FMVSS) ISO 3795 >=1.0 mm mm/min passed
Coefficient of linear thermal expansion, normal ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.6
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.4
Glow wire test (GWFI) [UL recognition] IEC 60695-2-12 1.5 mm °C 960
Glow wire test (GWFI) [UL recognition] IEC 60695-2-12 3.0 mm °C 960
Glow wire test (GWFI) [UL recognition] IEC 60695-2-12 0.75 mm °C 960
Glow wire test (GWIT) IEC 60695-2-13 1.5 mm °C 800
Glow wire test (GWIT) IEC 60695-2-13 3.0 mm °C 875
Oxygen index ISO 4589-2 Method A % 37
Relative temperature index (Electric strength) [UL recognition] UL 746B 0.75 mm °C 80
Relative temperature index (Tensile impact strength) [UL recognition] UL 746B 0.75 mm °C 80
Relative temperature index (Tensile strength) [UL recognition] UL 746B 0.75 mm °C 80
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 132
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 142
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 141
Property Name Standard Test condition Unit Value
Charpy impact strength ISO 179/1eU 23 °C kJ/m² > 100C
Charpy notched impact strength ISO 21305/based on ISO 179/1eA 23 °C/ 3 mm kJ/m² 8C
Flexural modulus ISO 178 2 mm/min MPa 3700
Flexural strain at flexural strength ISO 178 2 mm/min % 5.8
Flexural strength ISO 178 2 mm/min MPa 105
Flexural stress at 3.5 % strain ISO 178 2 mm/min MPa 90
Puncture energy ISO 6603-2 23 °C J 16
Puncture impact properties - maximum force ISO 6603-2 23 °C N 3200
Strain at break ISO 527-1,-2 5 mm/min % 10
Stress at break ISO 527-1,-2 5 mm/min MPa 45
Tensile modulus ISO 527-1,-2 1 mm/min MPa 3900
Yield strain ISO 527-1,-2 5 mm/min % 4.5
Yield stress ISO 527-1,-2 5 mm/min MPa 60
Property Name Standard Test condition Unit Value
Melt mass-flow rate ISO 1133 300 °C/ 1.2 kg g/10 min 16.5
Melt volume-flow rate ISO 1133 300 °C/ 1.2 kg cm³/10 min 15
Molding shrinkage, normal ISO 294-4 60x60x2 mm/ 500 bar % 0.45
Molding shrinkage, parallel ISO 294-4 60x60x2 mm/ 500 bar % 0.5
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 175
Comparative tracking index CTI M IEC 60112 Solution B Rating 125M
Dissipation factor IEC 60250 1 MHz 10^-4^ 90
Dissipation factor IEC 60250 100 Hz 10^-4^ 10
Electrical strength IEC 60243-1 1 mm kV/mm 36
Relative permittivity IEC 60250 1 MHz 3.2
Relative permittivity IEC 60250 100 Hz 3.2
Surface resistivity IEC 60093 Ohm 1E16
Volume resistivity IEC 60093 Ohm*m 1E14
Property Name Standard Test condition Unit Value
Injection molding - Injection velocity ISO 294 mm/s 200
Injection molding - Melt temperature ISO 294 °C 300
Injection molding - Mold temperature ISO 294 °C 110
Property Name Standard Test condition Unit Value
Bulk density ISO 60 Pellets kg/m³ 640
Density ISO 1183-1 kg/m³ 1270
Glass fiber content b.o. ISO 3451-1 Method A % 10
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.1
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.3

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Viscosity Shear Rate Makrolon® GF9002 (Multipoint Data Sheet) Viskosität Schergeschwindigkeit Makrolon® GF9002 (Multipoint Data Sheet)
Specific Volume-Temperature (pvT) Makrolon® GF9002 (Multipoint Data Sheet) Spezifisches Volumen-Temperatur (pvT) Makrolon® GF9002 (Multipoint Data Sheet)

Do you want to know more about Makrolon® GF9002?
Get in touch with our experts!

Contact form image Zoe

How would you describe yourself?

What type of material are you interested in?

What type of inquiry is this?

How can we contact you?

* Mandatory Fields

Form data successfully sent

Compare