Makrolon® FR6011
medium viscosity; impact modified; UV stabilized; flame retardant; improved chemical resistance compared to standard Makrolon grades; electrical/electronic; housing parts
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Dry Air Drying Temperature | - | °C | 120 | |
Dry Air Drying Time | - | h | 4 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Burning behavior UL 94 | UL 94 | 1.0 mm | Class | V-1 |
Burning behavior UL 94 | UL 94 | 1.5 mm | Class | V-0 |
Glow wire test (GWFI) | IEC 60695-2-12 | 1.0 mm | °C | 960 |
Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 960 |
Glow wire test (GWIT) | IEC 60695-2-13 | 1.0 mm | °C | 875 |
Glow wire test (GWIT) | IEC 60695-2-13 | 1.5 mm | °C | 850 |
Resistance to heat (ball pressure test) | IEC 60695-10-2 | °C | 125 | |
Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 129 |
Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 115 |
Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 138 |
Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 136 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
Flexural modulus | ISO 178 | 2 mm/min | MPa | 2250 |
Flexural strength | ISO 178 | 2 mm/min | MPa | 89 |
Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 70 P |
Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 20 C |
Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | >50 |
Puncture energy | ISO 6603-2 | -30 °C | J | 57 |
Puncture energy | ISO 6603-2 | 23 °C | J | 51 |
Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 6200 |
Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5000 |
Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2250 |
Yield strain | ISO 527-1,-2 | 50 mm/min | % | 5.9 |
Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 60 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C | Pa*s | 320 |
Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 4 |
Melt volume-flow rate | ISO 1133 | 300 °C/ 5 kg | cm³/10 min | 25 |
Molding shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience | % | 0.6 - 0.8 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Injection molding - Melt temperature | ISO 294 | °C | 300 | |
Injection molding - Mold temperature | ISO 294 | °C | 90 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Density | ISO 1183-1 | kg/m³ | 1190 | |
Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.12 |
Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.36 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com