- Plastics
Makrolon® FP2987
high viscosity; MVR (300 °C/1.2 kg) 9.0 cm³/10 min
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- UV stable, Optical quality
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 280 - 290 | |
| Barrel Temperatures - Middle | - | °C | 270 - 280 | |
| Barrel Temperatures - Nozzle | - | °C | 290 - 300 | |
| Barrel Temperatures - Rear | - | °C | 250 - 260 | |
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 2 - 3 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 280 - 320 | |
| Moisture Content max. (%) | - | % | <= 0,02 | |
| Mold Temperatures | - | °C | 80 - 120 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 300 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 122 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 142 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C | kJ/m² | 75 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -20 °C | kJ/m² | 14 |
| Puncture energy | ISO 6603-2 | -30 °C | J | 67 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 62 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 6500 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5700 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 125 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 75 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2350 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 66 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 9.0 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 300 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com