Makrolon® AX2675

MVR (300 °C/1.2 kg) 12 cm³/10 min; medium viscosity; easy release; automotive exterior roof trim + pillar appliques; developed for high-gloss surfaces with highest requirements; for the use in combination with hard coatings

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • Polycarbonate

Material

No data available

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 280 - 290
Barrel Temperatures - Middle - °C 270 - 280
Barrel Temperatures - Nozzle - °C 290 - 300
Barrel Temperatures - Rear - °C 250 - 260
Dry Air Drying Temperature - °C 120 - 120
Dry Air Drying Time - h 2 - 3
Hold Pressure (% of injection pressure) - % 50 - 75
Melt Temperatures - °C 280 - 320
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 80 - 120
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt Temperature - °C 300
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Application of flame from small burner DIN 53438-1,-3 Method K and F; 2.0 mm Class K1, F1
Burning rate (US-FMVSS) ISO 3795 >=1.0 mm mm/min passed
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.65
Coefficient of linear thermal expansion, transverse ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.65
Flash ignition temperature ASTM D1929 °C 480
Glass transition temperature ISO 11357-1,-2 10 °C/min °C 143
Relative temperature index (Electric strength) UL 746B 1.5 mm °C 125
Relative temperature index (Tensile impact strength) UL 746B 1.5 mm °C 115
Relative temperature index (Tensile strength) UL 746B 1.5 mm °C 125
Resistance to heat (ball pressure test) IEC 60695-10-2 °C 135
Self ignition temperature ASTM D1929 °C 550
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 136
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 124
Thermal conductivity, cross-flow ISO 8302 23 °C; 50 % r. h. W/(m*K) 0.2
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 144
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 143 - 143
Property Name Standard Test condition Unit Value
Ball indentation hardness ISO 2039-1 N/mm² 115
Charpy impact strength ISO 179-1eU -30 °C kJ/m² N
Charpy impact strength ISO 179-1eU -60 °C kJ/m² N
Charpy impact strength ISO 179-1eU 23 °C kJ/m² N
Charpy notched impact strength ISO 7391/b.o. ISO 179-1eA -30 °C; 3 mm kJ/m² 16C
Charpy notched impact strength ISO 7391/b.o. ISO 179-1eA 23 °C; 3 mm kJ/m² 70P
Flexural modulus ISO 178 2 mm/min MPa 2400 - 2400
Flexural strain at flexural strength ISO 178 2 mm/min % 7.1 - 7.1
Flexural strength ISO 178 2 mm/min MPa 98
Flexural stress at 3.5 % strain ISO 178 2 mm/min MPa 74 - 74
Izod notched impact strength ISO 7391/b.o. ISO 180-A 23 °C; 3 mm kJ/m² 70P
Izod notched impact strength ISO 7391/b.o. ISO 180-A -30 °C; 3 mm kJ/m² 14C
Nominal strain at break ISO 527-1,-2 50 mm/min % > 50
Puncture energy ISO 6603-2 -30 °C J 60
Puncture energy ISO 6603-2 23 °C J 55 - 55
Puncture maximum force ISO 6603-2 -30 °C N 6100
Puncture maximum force ISO 6603-2 23 °C N 5200 - 5200
Strain at break b.o. ISO 527-1,-2 50 mm/min % 120
Stress at break ISO 527-1,-2 50 mm/min MPa 69
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2400 - 2400
Yield strain ISO 527-1,-2 50 mm/min % 6
Yield stress ISO 527-1,-2 50 mm/min MPa 65
Property Name Standard Test condition Unit Value
Melt mass-flow rate ISO 1133 300 °C; 1.2 kg g/10 min 13
Melt volume-flow rate ISO 1133 300 °C; 1.2 kg cm³/10 min 12
Molding shrinkage, normal ISO 294-4 60x60x2 mm; 500 bar % 0.75
Molding shrinkage, parallel ISO 294-4 60x60x2 mm; 500 bar % 0.7
Molding shrinkage, parallel/normal b.o. ISO 2577 Value range based on general practical experience % 0.6 - 0.8
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 250
Comparative tracking index CTI M IEC 60112 Solution B Rating 125M
Dissipation factor IEC 60250 1 MHz 10^-4^ 90
Dissipation factor IEC 60250 100 Hz 10^-4^ 5
Electrical strength IEC 60243-1 1 mm kV/mm 34
Electrolytic corrosion IEC 60426 Rating A1
Relative permittivity IEC 60250 1 MHz 3.0
Relative permittivity IEC 60250 100 Hz 3.1
Surface resistivity IEC 60093 Ohm 1E16
Volume resistivity IEC 60093 Ohm*m 1E14
Property Name Standard Test condition Unit Value
Injection molding-Injection velocity ISO 294 mm/s 200
Injection molding-Melt temperature ISO 294 °C 290 - 290
Injection molding-Mold temperature ISO 294 °C 80 - 80
Property Name Standard Test condition Unit Value
Bulk density ISO 60 Pellets kg/m³ 660
Density ISO 1183-1 kg/m³ 1200 - 1200
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.12
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.3
Water vapor permeability ISO 15106-1 23 °C; 85 % RH; 100 µm film g/(m²*24 h) 15

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Do you want to know more about Makrolon® AX2675?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

1 product to compare