Makrolon® Ai2215 EL
MVR (300 °C/1.2 kg) 34 cm³/10 min; low viscosity; easy release; edge lighting material for light guides and optical parts; Automotive interior
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 260 - 270 | |
| Barrel Temperatures - Middle | - | °C | 250 - 260 | |
| Barrel Temperatures - Nozzle | - | °C | 260 - 270 | |
| Barrel Temperatures - Rear | - | °C | 230 - 240 | |
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 2 - 3 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 250 - 300 | |
| Moisture Content max. (%) | - | % | <= 0.02 | |
| Mold Temperatures | - | °C | 80 - 120 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 270 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Glass transition temperature | ISO 11357-1,-2 | 10 °C/min | °C | 145 |
| Oxygen index | ISO 4589-2 | Method A | % | 28 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 138 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 125 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 146 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 145 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | -30 °C | kJ/m² | N |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | -30 °C/ 3 mm | kJ/m² | 15C |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | 23 °C/ 3 mm | kJ/m² | 60P |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 55P |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -20 °C/ 3 mm | kJ/m² | 13C |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | > 50 |
| Puncture energy | ISO 6603-2 | -30 °C | J | 55 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 50 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 5900 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 4900 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 125 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 60 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2200 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 63 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 4 mm | % | >85 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 34 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³/ 500 bar | % | 0.7 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³/ 500 bar | % | 0.69 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 280 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Bulk density | ISO 60 | Pellets | kg/m³ | 660 |
| Density | ISO 1183-1 | kg/m³ | 1190 | |
| Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.12 |
| Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.3 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com