Makrolon® 1205
Formerly Makrolon KU1-1205; MVR (300 °C/1.2 kg) 6.0 cm³/10 min; flame retardant; high viscosity; solid sheet; aircraft construction; automotive construction; railway construction
i
Market Switch
Selection will influence the results you get.
About
Product Types
- Polycarbonate
Material
- Plastics
- Transparent, Flame retardant
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 2.0 mm | °C | 960 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 960 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 140 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 125 |
| Vertical Bunsen burner test | FAR 25.853(b) | 1.0 mm/ 12 s | passed | |
| Vertical Bunsen burner test | FAR 25.853(a) | 1.0 mm/ 60 s | passed | |
| Vertical Bunsen burner test | FAR 25.853(a) | 1.5 mm/ 60 s | passed | |
| Vertical Bunsen burner test | FAR 25.853(b) | 1.5 mm/ 12 s | passed | |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 147 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | -30 °C | kJ/m² | N |
| Charpy impact strength | ISO 179/1eU | -60 °C | kJ/m² | N |
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 65P |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 15C |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | > 50 |
| Puncture energy | ISO 6603-2 | -30 °C | J | 70 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 65 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 6700 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5800 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 125 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 70 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2350 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6.5 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 63 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt mass-flow rate | ISO 1133 | 300 °C/ 1.2 kg | g/10 min | 6.5 |
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 6 |
| Molding shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience | % | 0.6 - 0.8 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 300 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Bulk density | ISO 60 | Pellets | kg/m³ | 660 |
| Density | ISO 1183-1 | kg/m³ | 1200 |