Impranil® DAH
Anionic, aromatic polyether-polyurethane dispersionUsed as a flexible tie coat in the manufacture of materials for outerwear, bags/luggage, shoes and athletic shoes.
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
Impranil® DAH is an anionic, aromatic polyether-polyurethane dispersion.
Impranil® DAH is used as a flexible tie coat applied by the transfer coating process in the manufacture of materials for outerwear, bags/luggage, shoes and athletic shoes.
Impranil® DAH is used as a flexible tie coat applied by the transfer coating process in the manufacture of materials for outerwear, bags/luggage, shoes and athletic shoes.
Storage Conditions
- Storage in original sealed Covestro container.
- Recommended storage temperature: 5 - 30°C.
- Protect from frost, heat and foreign material.
General information: The product cannot be used if it has been frozen. The containers must be well closed to prevent the evaporation of water which may result in the formation of a non-redispersible film.
- Recommended storage temperature: 5 - 30°C.
- Protect from frost, heat and foreign material.
General information: The product cannot be used if it has been frozen. The containers must be well closed to prevent the evaporation of water which may result in the formation of a non-redispersible film.
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Characteristics
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Density at 23 °C | DIN 53217/3 | g/cm3 | 1.1 |
Specifications
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Viscosity at 23 °C, D = 40 s^-1 | DIN EN 3219/A.3 | mPa*s | 50 - 800 |
| pH | DIN ISO 976 | 8 ± 1 | |
| Non-volatile content (0.9 - 1.1 g / 1h /125 °C, convection oven) | DIN EN ISO 3251 | 35 ± 1 |