Bayblend® T70 X

(PC+ABS)-Blend; General Purpose Grade; Vicat/B 120 temperature = 124 °C; good injection molding processing behaviour (easy flowing); excellent long-term ageing behaviour under humid conditions; good painting performance; improved chemical resistance; low VOC emissions and odour

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

No data available

Material

No data available

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Dry Air Drying Temperature - °C 95 - 110
Dry Air Drying Time - h 4
Melt temperatures - °C 270 - 290
Moisture Content max. (%) - % 0.01
Mold Temperatures - °C 70 - 90
Standard Melt temperature - °C 280
Property Name Standard Test condition Unit Value
Burning behavior UL 94 UL 94 0.85 mm Class HB (Covestro-Test)
Coefficient of linear thermal expansion, normal ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.7
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.7
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 125
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 103
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 124
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 122
Property Name Standard Test condition Unit Value
Charpy impact strength ISO 179/1eU -30 °C kJ/m² N
Charpy impact strength ISO 179/1eU 23 °C kJ/m² N
Charpy notched impact strength ISO 179/1eA -30 °C kJ/m² 50
Charpy notched impact strength ISO 179/1eA 23 °C kJ/m² 60
Izod impact strength ISO 180/U -30 °C kJ/m² N
Izod impact strength ISO 180/U 23 °C kJ/m² N
Izod notched impact strength ISO 180/A 23 °C kJ/m² 55
Izod notched impact strength ISO 180/A -30 °C kJ/m² 45
Nominal strain at break ISO 527-1,-2 50 mm/min % 100
Puncture energy ISO 6603-2 -30 °C J 53
Puncture energy ISO 6603-2 23 °C J 48
Puncture impact properties - maximum force ISO 6603-2 -30 °C N 5200
Puncture impact properties - maximum force ISO 6603-2 23 °C N 4300
Stress at break ISO 527-1,-2 50 mm/min MPa 53
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2250
Yield strain ISO 527-1,-2 50 mm/min % 4.7
Yield stress ISO 527-1,-2 50 mm/min MPa 53
Property Name Standard Test condition Unit Value
Melt viscosity b.o. ISO 11443-A 1000 s^-1^/ 260 °C Pa*s 210
Melt volume-flow rate ISO 1133 260 °C/ 5 kg cm³/10 min 18
Molding shrinkage, normal ISO 294-4 60x60x2 mm/ 260 °C / MT 80 °C/ 500 bar % 0.55 - 0.75
Molding shrinkage, parallel ISO 294-4 60x60x2 mm/ 260 °C / MT 80 °C/ 500 bar % 0.55 - 0.75
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 200
Dissipation factor IEC 60250 1 MHz 10^-4^ 90
Dissipation factor IEC 60250 100 Hz 10^-4^ 25
Electrical strength IEC 60243-1 1 mm kV/mm 40
Relative permittivity IEC 60250 1 MHz 3.0
Relative permittivity IEC 60250 100 Hz 2.9
Surface resistivity IEC 60093 Ohm 1E+16
Volume resistivity IEC 60093 Ohm*m 1E+16
Property Name Standard Test condition Unit Value
Injection molding - Injection velocity ISO 294 mm/s 240
Injection molding - Melt temperature ISO 294 °C 280
Injection molding - Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1130
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.1
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.4

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Related topics

Do you want to know more about Bayblend® T70 X?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

Compare