Bayblend® FR3016 W

(PC-I)-Blend; flame retardant; Vicat/B 120 temperature = 101 °C; UL-recognition 94 V-0 at 0.75mm; rated f1 per UL746 C "Outdoor Suitability"; improved colorability compared to other PC+ASA grades

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

No data available

Material

No data available

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 230 - 240
Barrel Temperatures - Middle - °C 225 - 235
Barrel Temperatures - Nozzle - °C 255 - 265
Barrel Temperatures - Rear - °C 220 - 230
Dry Air Drying Temperature - °C 80
Dry Air Drying Time - h 4
Hold Pressure (% of injection pressure) - % 50 - 75
Melt temperatures - °C 240 - 270
Moisture Content max. (%) - % >=0.02
Mold Temperatures - °C 60 - 90
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt temperature - °C 260
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 [UL recognition] UL 94 0.75 mm Class V-0
Coefficient of linear thermal expansion, normal ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.65
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.65
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 93
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 83
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 101
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 98
Property Name Standard Test condition Unit Value
Flexural modulus ISO 178 2 mm/min MPa 2700
Flexural strength ISO 178 2 mm/min MPa 102
Izod impact strength ISO 180/U -30 °C kJ/m² N
Izod impact strength ISO 180/U 23 °C kJ/m² N
Izod notched impact strength ISO 180/A 23 °C kJ/m² 12
Izod notched impact strength ISO 180/A -30 °C kJ/m² 5
Nominal strain at break ISO 527-1,-2 50 mm/min % >50
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2700
Yield strain ISO 527-1,-2 50 mm/min % 4.1
Yield stress ISO 527-1,-2 50 mm/min MPa 64
Property Name Standard Test condition Unit Value
Melt viscosity b.o. ISO 11443-A 1000 s^-1^/ 260 °C Pa*s 180
Melt volume-flow rate ISO 1133 240 °C/ 5 kg cm³/10 min 32
Molding shrinkage, normal b.o. ISO 2577 150x105x3 mm/ 240 °C / MT 80 °C % 0.5 - 0.7
Molding shrinkage, parallel b.o. ISO 2577 150x105x3 mm/ 240 °C / MT 80 °C % 0.5 - 0.7
Property Name Standard Test condition Unit Value
Electrical strength IEC 60243-1 1 mm kV/mm 35
Relative permittivity IEC 60250 1 MHz 3.1
Relative permittivity IEC 60250 100 Hz 3.2
Surface resistivity IEC 60093 Ohm 1E16
Volume resistivity IEC 60093 Ohm*m 1E14
Property Name Standard Test condition Unit Value
Injection molding - Injection velocity ISO 294 mm/s 240
Injection molding - Melt temperature ISO 294 °C 240
Injection molding - Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1210
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.2
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.5

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Related topics

Do you want to know more about Bayblend® FR3016 W?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

Compare