Bayblend® ET3032 FR
Rubber modified PC blend; 10 % mineral filled; flame retardant; Vicat/B 120 temperature = 108 °C; extrusion grade; good extrusion and vacuum-forming behaviour; UL-recognition 94 V-0 at 0.75mm; glow wire temperature (GWFI): 960 °C at 2.0 mm
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- Flame retardant, Dimensionally stable
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 [UL recognition] | UL 94 | 0.75 mm | Class | V-0 |
| Burning behavior UL 94-5V | UL 94 | 2.0 mm | Class | 5VB (Covestro Test) |
| Burning behavior UL 94-5V | UL 94 | 3.0 mm | Class | 5VA (Covestro Test) |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.59 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.48 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 94 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 108 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 106 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 9 |
| Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 7 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 15 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 50 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 3950 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 4 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 63 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 260 °C | Pa*s | 380 |
| Melt volume-flow rate | ISO 1133 | 260 °C/ 5 kg | cm³/10 min | 10 |
| Molding shrinkage, normal | b.o. ISO 2577 | 150x105x3 mm³/ 260 °C / MT 80 °C | % | 0.4 - 0.5 |
| Molding shrinkage, parallel | b.o. ISO 2577 | 150x105x3 mm³/ 260 °C / MT 80 °C | % | 0.4 - 0.5 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 240 | |
| Injection molding - Melt temperature | ISO 294 | °C | 260 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1300 | |
| Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.2 |
| Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.5 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com
-
Secant modulus - Strain Bayblend® ET3032 FR (Multipoint Data Sheet) Sekantenmodul-Dehnung Bayblend® ET3032 FR (Multipoint Data Sheet)
-
Stress-Strain Bayblend® ET3032 FR (Multipoint Data Sheet) Spannung-Dehnung Bayblend® ET3032 FR (Multipoint Data Sheet)