Makrolon® GF9417
polycarbonate; MVR (300 °C/1.2 kg) 6.0 cm³/10 min; 10 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; UV stabilized; easy release
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Dry Air Drying Temperature | - | °C | 120 | |
Dry Air Drying Time | - | h | 2 - 3 | |
Melt temperatures | - | °C | 280 - 320 | |
Mold Temperatures | - | °C | 110 | |
Standard Melt temperature | - | °C | 300 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Burning behavior UL 94 (1.5 mm) [UL recognition] | UL 94 | Class | V-0 | |
Burning behavior UL 94-5V [UL recognition] | UL 94 | 3.0 mm | Class | 5VA |
Glow wire test (GWFI) | IEC 60695-2-12 | 0.75 mm | °C | 960 |
Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 960 |
Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 960 |
Glow wire test (GWIT) | IEC 60695-2-13 | 0.75 mm | °C | 825 |
Glow wire test (GWIT) | IEC 60695-2-13 | 1.5 mm | °C | 850 |
Glow wire test (GWIT) | IEC 60695-2-13 | 3.0 mm | °C | 850 |
Oxygen index | ISO 4589-2 | Method A | % | 36 |
Relative temperature index (Electric strength) [UL recognition] | UL 746B | 1.5 mm | °C | 125 |
Relative temperature index (Tensile impact strength) [UL recognition] | UL 746B | 1.5 mm | °C | 125 |
Relative temperature index (Tensile strength) [UL recognition] | UL 746B | 1.5 mm | °C | 125 |
Resistance to heat (ball pressure test) | IEC 60695-10-2 | °C | 130 | |
Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 144 |
Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 137 |
Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 144 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | 150C |
Nominal strain at break | ISO 527-1,-2 | 5 mm/min | % | 10 |
Puncture energy | ISO 6603-2 | -30 °C | J | 15 |
Puncture energy | ISO 6603-2 | 23 °C | J | 25 |
Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 3700 |
Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 3900 |
Strain at break | ISO 527-1,-2 | 5 mm/min | % | 15 |
Stress at break | ISO 527-1,-2 | 5 mm/min | MPa | 45 |
Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 3800 |
Yield strain | ISO 527-1,-2 | 5 mm/min | % | 4.8 |
Yield stress | ISO 527-1,-2 | 5 mm/min | MPa | 62 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C | Pa*s | 320 |
Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 6 |
Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³ | % | 0.45 |
Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³ | % | 0.6 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 175 |
Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 37 |
Surface resistivity | IEC 62631-3-2 | Ohm | 8E+15 | |
Volume resistivity | IEC 62631-3-1 | Ohm*m | 3E+14 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
Injection molding - Melt temperature | ISO 294 | °C | 300 | |
Injection molding - Mold temperature | ISO 294 | °C | 110 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Density | ISO 1183-1 | kg/m³ | 1270 | |
Glass fiber content | b.o. ISO 3451-1 | Method A | % | 10 |