Makrolon® FR6040

polycarbonate; easy release; UV stabilized; flame retardant; toughness at low temperature; Information technology; electrical/electronic

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

No data available

Material

No data available

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Dry Air Drying Temperature - °C 120
Property Name Standard Test condition Unit Value
Burning behavior UL 94 (1.5 mm) [UL recognition] UL 94 Class V-0
Burning behavior UL 94-5V UL 94 2.0 mm Class 5 VB
Coefficient of linear thermal expansion, normal ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.68
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.63
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 129
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 114
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 135
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 134
Property Name Standard Test condition Unit Value
Ball indentation hardness ISO 2039-1 N/mm² 107
Charpy impact strength ISO 179/1eU -30 °C kJ/m² N
Charpy impact strength ISO 179/1eU 23 °C kJ/m² N
Charpy notched impact strength ISO 21305/based on ISO 179/1eA 23 °C kJ/m² 65
Charpy notched impact strength ISO 21305/based on ISO 179/1eA -10 °C kJ/m² 60
Charpy notched impact strength ISO 21305/based on ISO 179/1eA -30 °C kJ/m² 50
Charpy notched impact strength ISO 21305/based on ISO 179/1eA -20 °C kJ/m² 55
Flexural modulus ISO 178 2 mm/min MPa 2300
Flexural strain at flexural strength ISO 178 2 mm/min % 6.8
Flexural strength ISO 178 2 mm/min MPa 90
Flexural stress at 3.5 % strain ISO 178 2 mm/min MPa 70
Izod impact strength ISO 180/U -30 °C kJ/m² N
Izod notched impact strength ISO 21305/based on ISO 180/A 23 °C kJ/m² 60
Izod notched impact strength ISO 21305/based on ISO 180/A -20 °C kJ/m² 50
Izod notched impact strength ISO 21305/based on ISO 180/A -30 °C kJ/m² 45
Izod notched impact strength ISO 21305/based on ISO 180/A -10 °C kJ/m² 55
Puncture energy ISO 6603-2 23 °C J 45
Puncture impact properties - maximum force ISO 6603-2 23 °C N 4800
Strain at break b.o. ISO 527-1,-2 50 mm/min % =>50
Stress at break ISO 527-1,-2 50 mm/min MPa 60
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2200
Yield strain ISO 527-1,-2 50 mm/min % 5.6
Yield stress ISO 527-1,-2 50 mm/min MPa 55
Property Name Standard Test condition Unit Value
Melt viscosity b.o. ISO 11443-A 1000 s^-1^/ 300 °C Pa*s 225
Melt volume-flow rate ISO 1133 300 °C/ 1.2 kg cm³/10 min 10
Molding shrinkage, normal ISO 294-4 60x60x2 mm % 0.7
Molding shrinkage, parallel ISO 294-4 60x60x2 mm % 0.75
Property Name Standard Test condition Unit Value
Surface resistivity IEC 60093 Ohm 1E+17
Volume resistivity IEC 60093 Ohm*m 1E+16
Property Name Standard Test condition Unit Value
Injection molding - Melt temperature ISO 294 °C 280 - 300
Injection molding - Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1200
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.18

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com

Related topics

Do you want to know more about Makrolon® FR6040?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

Compare