Makrolon® FR6019 CTI
MVR (300 °C/1.2 kg) 13 cm³/10 min; medium viscosity; flame retardant; UL 94V-0/1.5 mm; CTI = 600 V; developed for high voltage application such as electric vehicles and battery packaging; for available colors, please contact us
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Dry Air Drying Temperature | - | °C | 120 | |
Dry Air Drying Time | - | h | 4 | |
Melt temperatures | - | °C | 280 - 310 | |
Standard Melt temperature | - | °C | 90 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Burning behavior UL 94 (1.5 mm) [UL recognition] | UL 94 | Class | V-0 | |
Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.71 |
Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 960 |
Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 960 |
Glow wire test (GWIT) | IEC 60695-2-13 | 1.5 mm | °C | 825 |
Glow wire test (GWIT) | IEC 60695-2-13 | 3.0 mm | °C | 825 |
Resistance to heat (ball pressure test) | IEC 60695-10-2 | °C | 120 | |
Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 125 |
Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 112 |
Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 131 |
Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 130 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Ball indentation hardness | ISO 2039-1 | N/mm² | 128 | |
Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | 23 °C | kJ/m² | 11 |
Flexural modulus | ISO 178 | 2 mm/min | MPa | 2450 |
Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 7 |
Flexural strength | ISO 178 | 2 mm/min | MPa | 99 |
Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 76 |
Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C | kJ/m² | 9 |
Nominal strain at break | ISO 527-1,-2 | 5 mm/min | % | >50 |
Puncture energy | ISO 6603-2 | 23 °C | J | 58 |
Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5200 |
Strain at break | ISO 527-1,-2 | 5 mm/min | % | 119 |
Stress at break | ISO 527-1,-2 | 5 mm/min | MPa | 66 |
Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2470 |
Yield strain | ISO 527-1,-2 | 5 mm/min | % | 6 |
Yield stress | ISO 527-1,-2 | 5 mm/min | MPa | 66 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C | Pa*s | 200 |
Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 13 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 600 |
Electrical strength | b.o. IEC 60243-1 | kV/mm | 31 | |
Surface resistivity | IEC 62631-3-2 | Ohm | 5 E+16 | |
Volume resistivity | IEC 62631-3-1 | Ohm*m | 4 E+17 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Density | ISO 1183-1 | kg/m³ | 1200 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com