Makrolon® 6487 R30 CQ
MVR (300 °C/1.2 kg) 11 cm³/10 min; contains 30 % pre-consumer PC recyclate; flame retardant; UL 94V-0/1.5 mm; medium viscosity; UV stabilized; easy release; electrical/electronic
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 280 - 290 | |
| Barrel Temperatures - Middle | - | °C | 270 - 280 | |
| Barrel Temperatures - Nozzle | - | °C | 290 - 300 | |
| Barrel Temperatures - Rear | - | °C | 250 - 260 | |
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 2 - 3 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 280 - 320 | |
| Moisture Content max. (%) | - | % | <= 0.02 | |
| Mold Temperatures | - | °C | 80 - 120 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 300 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 [UL recognition] | UL 94 | 1.5 mm | Class | V-0 (bk) |
| Burning behavior UL 94 [UL recognition] | UL 94 | 3.0 mm | Class | V-0 (bk) |
| Burning behavior UL 94-5V | UL 94 | 3.0 mm | Class | 5VA (Covestro test) |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.0 mm | °C | 960 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 960 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 136 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 122 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 142 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 141 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 15 |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | > 50 |
| Puncture energy | ISO 6603-2 | -30 °C | J | 50 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 50 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 6100 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5200 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 110 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 67 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2350 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 67 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C | Pa*s | 270 |
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 11 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 225 (175) |
| Dissipation factor | IEC 60250 | 1 MHz | 10^-4^ | 96 |
| Dissipation factor | IEC 60250 | 100 Hz | 10^-4^ | 7 |
| Relative permittivity | IEC 60250 | 1 MHz | 3 | |
| Relative permittivity | IEC 60250 | 100 Hz | 3 | |
| Surface resistivity | IEC 60093 | Ohm | 2E16 | |
| Volume resistivity | IEC 60093 | Ohm*m | 9E16 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 300 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |