Makrolon® 6165 X

MVR (300 °C/1.2 kg) 28 cm³/10 min; flame retardant; UL 94V-0/1.2 mm; low viscosity; easy release

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • Polycarbonate

Material

Plastics
Flame retardant

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 280 - 290
Barrel Temperatures - Middle - °C 270 - 280
Barrel Temperatures - Nozzle - °C 290 - 300
Barrel Temperatures - Rear - °C 250 - 260
Dry Air Drying Temperature - °C 120
Dry Air Drying Time - h 2 - 3
Hold Pressure (% of injection pressure) - % 50 - 75
Melt Temperatures - °C 280 - 320
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 80 - 120
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt Temperature - °C 300
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 UL 94 1.2 mm Class V-0
Burning rate (US-FMVSS) ISO 3795 >=1.0 mm mm/min passed
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.65
Coefficient of linear thermal expansion, transverse ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.65
Flash ignition temperature ASTM D1929 °C 460
Glow wire test (GWFI) IEC 60695-2-12 1.5 mm °C 960
Glow wire test (GWFI) IEC 60695-2-12 3.0 mm °C 960
Oxygen index ISO 4589-2 Method A % 35
Relative temperature index (Electric strength) UL 746B 1.5 mm °C 125
Relative temperature index (Tensile impact strength) UL 746B 1.5 mm °C 115
Relative temperature index (Tensile strength) UL 746B 1.5 mm °C 125
Self ignition temperature ASTM D1929 °C 530
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 136
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 124
Thermal conductivity, cross-flow ISO 8302 23 °C; 50 % r. h. W/(m*K) 0.2
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 143
Property Name Standard Test condition Unit Value
Charpy impact strength ISO 179-1eU -30 °C kJ/m² N
Charpy impact strength ISO 179-1eU 23 °C kJ/m² N
Charpy notched impact strength ISO 7391/b.o. ISO 179-1eA -30 °C/ 3 mm kJ/m² 12C
Charpy notched impact strength ISO 7391/b.o. ISO 179-1eA 23 °C/ 3 mm kJ/m² 15C
Izod notched impact strength ISO 7391/b.o. ISO 180-A 23 °C/ 3 mm kJ/m² 15P(C)
Izod notched impact strength ISO 7391/b.o. ISO 180-A -30 °C/ 3 mm kJ/m² 11C
Nominal strain at break ISO 527-1,-2 50 mm/min % > 50
Puncture energy ISO 6603-2 23 °C J 45
Puncture maximum force ISO 6603-2 23 °C N 4800
Strain at break b.o. ISO 527-1,-2 50 mm/min % 120
Stress at break ISO 527-1,-2 50 mm/min MPa 55
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2350
Yield strain ISO 527-1,-2 50 mm/min % 6
Yield stress ISO 527-1,-2 50 mm/min MPa 65
Property Name Standard Test condition Unit Value
Melt mass-flow rate ISO 1133 300 °C/ 1.2 kg g/10 min 30
Melt volume-flow rate ISO 1133 300 °C/ 1.2 kg cm³/10 min 28
Molding shrinkage, normal ISO 294-4 60x60x2 mm/ 500 bar % 0.7
Molding shrinkage, parallel ISO 294-4 60x60x2 mm/ 500 bar % 0.65
Molding shrinkage, parallel/normal b.o. ISO 2577 Value range based on general practical experience % 0.5 - 0.7
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 225
Comparative tracking index CTI M IEC 60112 Solution B Rating 125M
Electrical strength IEC 60243-1 1 mm kV/mm 34
Relative permittivity IEC 60250 1 MHz 3.0
Relative permittivity IEC 60250 100 Hz 3.1
Surface resistivity IEC 60093 Ohm 1E16
Volume resistivity IEC 60093 Ohm*m 1E14
Property Name Standard Test condition Unit Value
Injection molding-Injection velocity ISO 294 mm/s 200
Injection molding-Melt temperature ISO 294 °C 280
Injection molding-Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Bulk density ISO 60 Pellets kg/m³ 640
Density ISO 1183-1 kg/m³ 1200
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.12
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.3

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download
Viscosity Shear Rate Makrolon® 6165 X (Multipoint Data Sheet) Viskosität Schergeschwindigkeit Makrolon® 6165 X (Multipoint Data Sheet)
Download

Do you want to know more about Makrolon® 6165 X?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

1 product to compare