- Plastics
Makroblend® UT215 M
(PC+PET) Blend, 5% mineral filled, easy flow, easy release, good impact strength, for automotive applications
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- Heat resistant, Dimensionally stable, Paintable
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Barrel Temperatures - Front | - | °C | 260 - 270 | |
Barrel Temperatures - Middle | - | °C | 240 - 250 | |
Barrel Temperatures - Nozzle | - | °C | 270 - 280 | |
Barrel Temperatures - Rear | - | °C | 220 - 230 | |
Dry Air Drying Temperature | - | °C | 110 | |
Dry Air Drying Time | - | h | 2 - 4 | |
Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
Melt temperatures | - | °C | 270 - 280 | |
Moisture Content max. (%) | - | % | <= 0.01 | |
Mold Temperatures | - | °C | 70 - 80 | |
Peripheral Screw Speed | - | m/s | 0.1 - 0.2 | |
Plastic Back Pressure (specific) | - | bar | 50 - 100 | |
Shot-to-Cylinder Size | - | % | 30 - 70 | |
Standard Melt temperature | - | °C | 270 | |
Vent Depth | - | mm | 0.02 - 0.03 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.6 |
Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.6 |
Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 130 |
Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 112 |
Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 140 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Charpy impact strength | ISO 179/1eU | -30 °C | kJ/m² | 200 |
Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
Charpy notched impact strength | ISO 179/1eA | 23 °C | kJ/m² | 6 |
Flexural modulus | ISO 178 | 2 mm/min | MPa | 3100 |
Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 5.8 |
Flexural strength | ISO 178 | 2 mm/min | MPa | 105 |
Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 90 |
Izod impact strength | ISO 180/1C | -30 °C | kJ/m² | 175 |
Izod impact strength | ISO 180/1C | 23 °C | kJ/m² | N |
Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 6 |
Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | 70 |
Puncture energy | ISO 6603-2 | 23 °C | J | 45 |
Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 4700 |
Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 50 |
Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 3050 |
Yield strain | ISO 527-1,-2 | 50 mm/min | % | 5 |
Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 65 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 270 °C | Pa*s | 205 |
Melt volume-flow rate | ISO 1133 | 270 °C/ 5 kg | cm³/10 min | 49 |
Molding shrinkage, normal | b.o. ISO 2577 | 150x105x3 mm³/ 270 °C / MT 70°C/ 600 bar | % | 0.60-0.75 |
Molding shrinkage, parallel | b.o. ISO 2577 | 150x105x3 mm³/ 270 °C / MT 70°C/ 600 bar | % | 0.60-0.75 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Drying time | ISO 294 | h | 4 - 6 | |
Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
Injection molding - Melt temperature | ISO 294 | °C | 270 | |
Injection molding - Mold temperature | ISO 294 | °C | 70 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Density | ISO 1183-1 | kg/m³ | 1270 | |
Filler content | b.o. ISO 3451-1 | Method A | % | 5 |
Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.2 |
Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.45 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com