Bayblend® T95 MF
(PC+ABS)-Blend; 9 % mineral filled; Vicat/B 120 temperature = 142 °C;; very good heat resistance; reduced coefficient of thermal expansion; tensile modulus = 3350 MPa
i
Market Switch
Selection will influence the results you get.
About
Product Types
- PC+ABS blend
Material
- Plastics
- Heat resistant, Dimensionally stable
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Barrel Temperatures - Front | - | °C | 250 - 280 | |
Barrel Temperatures - Middle | - | °C | 245 - 255 | |
Barrel Temperatures - Nozzle | - | °C | 275 - 285 | |
Barrel Temperatures - Rear | - | °C | 240 - 250 | |
Dry Air Drying Temperature | - | °C | 95 - 110 | |
Dry Air Drying Time | - | h | 4 | |
Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
Melt temperatures | - | °C | 270 - 290 | |
Moisture Content max. (%) | - | % | <= 0,02 | |
Mold Temperatures | - | °C | 70 - 90 | |
Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
Shot-to-Cylinder Size | - | % | 30 - 70 | |
Standard Melt temperature | - | °C | 280 | |
Vent Depth | - | mm | 0.025 - 0.075 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Burning behavior UL 94 | UL 94 | 0.85 mm | Class | HB (Bayer Test) |
Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.65 |
Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.55 |
Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 136 |
Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 124 |
Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 142 |
Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 140 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Izod impact strength | ISO 180/U | 23 °C | kJ/m² | >= 150 |
Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 9 |
Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 9 |
Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | >= 50 |
Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 52 |
Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 3350 |
Yield strain | ISO 527-1,-2 | 50 mm/min | % | 4.6 |
Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 66 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 260 °C | Pa*s | 400 |
Melt volume-flow rate | ISO 1133 | 260 °C/ 5 kg | cm³/10 min | 18 |
Molding shrinkage, normal | b.o. ISO 2577 | 150x105x3 mm³/ 260 °C / MT 80 °C | % | 0.5 - 0.7 |
Molding shrinkage, parallel | b.o. ISO 2577 | 150x105x3 mm³/ 260 °C / MT 80 °C | % | 0.5 - 0.7 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 200 |
Dissipation factor | IEC 60250 | 1 MHz | 10^-4^ | 90 |
Dissipation factor | IEC 60250 | 100 Hz | 10^-4^ | 15 |
Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 35 |
Relative permittivity | IEC 60250 | 1 MHz | 3.0 | |
Relative permittivity | IEC 60250 | 100 Hz | 3.2 | |
Surface resistivity | IEC 62631-3-2 | Ohm | 1E16 | |
Volume resistivity | IEC 62631-3-1 | Ohm*m | 1E14 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Injection molding - Injection velocity | ISO 294 | mm/s | 240 | |
Injection molding - Melt temperature | ISO 294 | °C | 260 | |
Injection molding - Mold temperature | ISO 294 | °C | 80 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Density | ISO 1183-1 | kg/m³ | 1240 | |
Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.2 |
Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.6 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com
-
Secant modulus - Strain Bayblend® T95 MF (Multipoint Data Sheet) Sekantenmodul-Dehnung Bayblend® T95 MF (Multipoint Data Sheet)
-
Viscosity Shear Rate Bayblend® T95 MF (Multipoint Data Sheet) Viskosität Schergeschwindigkeit Bayblend® T95 MF (Multipoint Data Sheet)
-
Stress-Strain Bayblend® T95 MF (Multipoint Data Sheet) Spannung-Dehnung Bayblend® T95 MF (Multipoint Data Sheet)