Submit
  • Plastics

Bayblend® FR3050

(PC+ABS)-Blend; flame retardant; high heat resistant injection molding grade; improved chemical resistance and stress cracking behavior compared to Bayblend® FR1514; Vicat/B 120 temperature = 136 °C; UL recognition 94 V-1 at 1.0 mm

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • PC+ABS blend

Material

Plastics
Impact resistant, Chemical resistant, Heat resistant

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 230 - 240
Barrel Temperatures - Middle - °C 225 - 235
Barrel Temperatures - Nozzle - °C 255 - 265
Barrel Temperatures - Rear - °C 220 - 230
Dry Air Drying Temperature - °C 80 - 80
Dry Air Drying Time - h 4 - 4
Hold Pressure (% of injection pressure) - % 50 - 75
Melt Temperatures - °C 240 - 270
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 60 - 90
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt Temperature - °C 260
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 UL 94 1.0 mm Class V-1
Burning behavior UL 94 (1.5 mm) UL 94 1.5 mm Class V-0
Burning behavior UL 94-5V UL 94 2.0 mm Class 5VB
Burning behavior UL 94-5V UL 94 3.0 mm Class 5VA
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.68
Coefficient of linear thermal expansion, transverse ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.68
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 126
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 115
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 136
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 134 - 134
Property Name Standard Test condition Unit Value
Izod impact strength ISO 180-U 23 °C kJ/m² N
Izod notched impact strength ISO 180-A 23 °C kJ/m² 55
Izod notched impact strength ISO 180-A -30 °C kJ/m² 15
Strain at break b.o. ISO 527-1,-2 50 mm/min % >50
Stress at break ISO 527-1,-2 50 mm/min MPa 60
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2400 - 2400
Yield strain ISO 527-1,-2 50 mm/min % 5
Yield stress ISO 527-1,-2 50 mm/min MPa 65
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 300
Dissipation factor IEC 60250 1 MHz 10^-4^ 80
Dissipation factor IEC 60250 100 Hz 10^-4^ 20
Electrical strength IEC 60243-1 1 mm kV/mm 35
Relative permittivity IEC 60250 1 MHz 3.1
Relative permittivity IEC 60250 100 Hz 3.2
Surface resistivity IEC 60093 Ohm 1E17
Volume resistivity IEC 60093 Ohm*m 1E15
Property Name Standard Test condition Unit Value
Injection molding-Injection velocity ISO 294 mm/s 240
Injection molding-Melt temperature ISO 294 °C 260 - 260
Injection molding-Mold temperature ISO 294 °C 80 - 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1190 - 1190
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.2
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.5

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Do you want to know more about Bayblend® FR3050?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

1 product to compare