Bayblend® FR3040 R35
(PC+ABS)-Blend; flame retardant; contains 35% post consumer PC recyclate for natural color; for notebooks and thinwall applications
i
Market Switch
Selection will influence the results you get.
About
Product Types
- PC+ABS blend
Material
- Foams
- Flame retardant
- Plastics
- CQ mechanical recycled
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 250 - 270 | |
| Barrel Temperatures - Middle | - | °C | 250 - 270 | |
| Barrel Temperatures - Nozzle | - | °C | 250 - 270 | |
| Barrel Temperatures - Rear | - | °C | 235 - 250 | |
| Dry Air Drying Temperature | - | °C | 85 | |
| Dry Air Drying Time | - | h | 4 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 250 - 270 | |
| Moisture Content max. (%) | - | % | <=0.02 | |
| Mold Temperatures | - | °C | 70 - 100 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 [UL recognition] | UL 94 | 0.75 mm | Class | V-0 (BK,WT,BL) |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 96 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 87 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 105 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 103 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Ball indentation hardness | ISO 2039-1 | New | N/mm² | 133 |
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Charpy notched impact strength | ISO 179/1eA | 23 °C | kJ/m² | 37 |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2700 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 5 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 101 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 87 |
| Izod impact strength | ISO 180/U | kJ/m² | N | |
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 35 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | >50 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 49 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2550 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 4.2 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 65 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 260 °C | Pa*s | 255 |
| Melt volume-flow rate | ISO 1133 | 240 °C/ 5 kg | cm³/10 min | 18 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³ | % | 0.5 - 0.7 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³ | % | 0.5 - 0.7 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Surface resistivity | IEC 62631-3-2 | Ohm | 1E17 | |
| Volume resistivity | IEC 62631-3-1 | Ohm*m | 1E16 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 240 | |
| Injection molding - Melt temperature | ISO 294 | °C | 260 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |