Submit
  • Plastics

Bayblend® FR3025

(PC+ABS)-Blend; flame retardant; mineral filled ; Vicat/B 120 temperature = 102 °C; UL recognition 94 V-0 at 1.2 mm; low warpage; improved stiffness and surface quality; for notebooks and thinwall applications

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • PC+ABS blend

Material

Plastics
Dimensionally stable, Flame retardant

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 270 - 300
Barrel Temperatures - Middle - °C 250 - 280
Barrel Temperatures - Nozzle - °C 270 - 300
Barrel Temperatures - Rear - °C 240 - 260
Dry Air Drying Temperature - °C 85
Dry Air Drying Time - h 2 - 4
Hold Pressure (% of injection pressure) - % 50 - 75
Melt temperatures - °C 270 - 300
Moisture Content max. (%) - % 0.02
Mold Temperatures - °C 65 - 100
Peripheral Screw Speed - m/s 0.1 - 0.3
Plastic Back Pressure (specific) - bar 50 - 100
Shot-to-Cylinder Size - % 30 - 70
Standard Melt temperature - °C 290
Vent Depth - mm 0.02 - 0.04
Property Name Standard Test condition Unit Value
Burning behavior UL 94 [UL recognition] UL 94 1.2 mm Class V-0
Burning behavior UL 94 [UL recognition] UL 94 0.75 mm Class V-1
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 96
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 90
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 102
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 100
Property Name Standard Test condition Unit Value
Charpy impact strength ISO 179/1eU -30 °C kJ/m² 45
Charpy impact strength ISO 179/1eU 23 °C kJ/m² 50
Charpy notched impact strength ISO 179/1eA -30 °C kJ/m² 4
Charpy notched impact strength ISO 179/1eA 23 °C kJ/m² 6
Izod impact strength ISO 180/U -30 °C kJ/m² 30
Izod impact strength ISO 180/U 23 °C kJ/m² 40
Izod notched impact strength ISO 180/A 23 °C kJ/m² 6
Izod notched impact strength ISO 180/A -30 °C kJ/m² 5
Puncture energy ISO 6603-2 -30 °C J 2
Puncture energy ISO 6603-2 23 °C J 13
Puncture impact properties - maximum force ISO 6603-2 -30 °C N 1100
Puncture impact properties - maximum force ISO 6603-2 23 °C N 2600
Strain at break b.o. ISO 527-1,-2 50 mm/min % 5.8
Stress at break ISO 527-1,-2 50 mm/min MPa 52
Tensile modulus ISO 527-1,-2 1 mm/min MPa 6300
Yield strain ISO 527-1,-2 50 mm/min % 2.8
Yield stress ISO 527-1,-2 50 mm/min MPa 59
Property Name Standard Test condition Unit Value
Melt viscosity b.o. ISO 11443-A 1000 s^-1^/ 260 °C Pa*s 230
Melt volume-flow rate ISO 1133 260 °C/ 5 kg cm³/10 min 27
Molding shrinkage, normal ISO 294-4 60x60x2 mm % 0.3
Molding shrinkage, parallel ISO 294-4 60x60x2 mm % 0.2
Property Name Standard Test condition Unit Value
Injection molding - Injection velocity ISO 294 mm/s 240
Injection molding - Melt temperature ISO 294 °C 260
Injection molding - Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1402
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.2
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.5

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Do you want to know more about Bayblend® FR3025?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

Compare