Bayblend® FR3020 W BBS910
PC Blend; impact modified; 5 % mineral filled; flame retardant; UV-stabilized; Vicat/B 120 temperature = 102 °C; flame-retardant;; UL recognition 94 V-0 (0.6mm); low smoke density
i
Market Switch
Selection will influence the results you get.
About
Product Types
- PC+ABS blend
Material
- Plastics
- Flame retardant, UV stable
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 | UL 94 | 0.6 mm | Class | V-0 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 102 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 12 |
| Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 8 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | > 50 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 51 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 3200 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 4 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 67 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 260 °C | Pa*s | 250 |
| Melt volume-flow rate | ISO 1133 | 260 °C/ 5 kg | cm³/10 min | 24 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 240 | |
| Injection molding - Melt temperature | ISO 294 | °C | 260 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |