Bayblend® FR3013

(PC+ABS)-Blend; flame retardant; impact modified; easy flowing; Vicat/B 120 temperature = 95°C; for: information technology

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • PC+ABS blend

Material

Plastics
Impact resistant, Flame retardant

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 230 - 240
Barrel Temperatures - Middle - °C 225 - 235
Barrel Temperatures - Nozzle - °C 255 - 265
Barrel Temperatures - Rear - °C 220 - 230
Dry Air Drying Temperature - °C 80
Dry Air Drying Time - h 4
Hold Pressure (% of injection pressure) - % 50 - 75
Melt temperatures - °C 240 - 270
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 60 - 80
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt temperature - °C 260
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 (1.5 mm) [UL recognition] UL 94 Class V-0
Burning behavior UL 94-5V [UL recognition] UL 94 1.5 mm Class 5VB
Coefficient of linear thermal expansion, normal ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.76
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.75
Oxygen index ISO 4589-2 Method A % 31
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 86
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 78
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 95
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 89
Property Name Standard Test condition Unit Value
Charpy notched impact strength ISO 179/1eA 23 °C kJ/m² 37
Flexural modulus ISO 178 2 mm/min MPa 2600
Flexural strength ISO 178 2 mm/min MPa 93
Izod impact strength ISO 180/U kJ/m² N
Izod notched impact strength ISO 180/A 23 °C kJ/m² 34
Izod notched impact strength ISO 180/A -30 °C kJ/m² 8
Strain at break b.o. ISO 527-1,-2 50 mm/min % 30
Stress at break ISO 527-1,-2 50 mm/min MPa 44
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2650
Yield strain ISO 527-1,-2 50 mm/min % 4
Yield stress ISO 527-1,-2 50 mm/min MPa 61
Property Name Standard Test condition Unit Value
Melt viscosity b.o. ISO 11443-A 1000 s^-1^/ 240 °C Pa*s 155
Melt volume-flow rate ISO 1133 240 °C/ 5 kg cm³/10 min 26
Molding shrinkage, normal b.o. ISO 2577 150x105x3 mm % 0.4 - 0.6
Molding shrinkage, normal ISO 294-4 60x60x2 mm % 0.4 - 0.6
Property Name Standard Test condition Unit Value
Surface resistivity IEC 60093 Ohm 5.0E17
Volume resistivity IEC 60093 Ohm*m 2.0E16
Property Name Standard Test condition Unit Value
Injection molding - Injection velocity ISO 294 mm/s 240
Injection molding - Melt temperature ISO 294 °C 240
Injection molding - Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1190

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com

Do you want to know more about Bayblend® FR3013?
Get in touch with our experts!

Contact form image Zoe

How would you describe yourself?

What type of material are you interested in?

What type of inquiry is this?

How can we contact you?

* Mandatory Fields

Form data successfully sent

Compare