Makrolon® TC629
polycarbonate; high viscosity; high temperature resistance; flame retardant; high thermal conductivity; electrically conductive; components for heat dissipation
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 300 - 320 | |
| Barrel Temperatures - Middle | - | °C | 290 - 310 | |
| Barrel Temperatures - Nozzle | - | °C | 310 - 330 | |
| Barrel Temperatures - Rear | - | °C | 280 - 300 | |
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 4 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 320 | |
| Moisture Content max. (%) | - | % | <= 0.02 | |
| Mold Temperatures | - | °C | 80 - 90 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Vent Depth | - | mm | 0.0025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 [UL recognition] | UL 94 | 2.0 mm | Class | V-0 (BK) |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.4 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.2 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 960 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 960 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 1.5 mm | °C | 900 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 3.0 mm | °C | 960 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 143 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 137 |
| Thermal conductivity, in-plane | ASTM E1461 | 23 °C; 50 % r. h. | W/(m*K) | 15 |
| Thermal conductivity, through-plane | ASTM E1461 | 23 °C; 50 % r. h. | W/(m*K) | 1.2 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 144 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | 6 |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 7400 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 1 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 58 |
| Strain at break | ISO 527-1,-2 | 5 mm/min | % | 1.0 |
| Stress at break | ISO 527-1,-2 | 5 mm/min | MPa | 41 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 6500 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 330 °C | Pa*s | 145 |
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C | Pa*s | 270 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³ | % | 0.1 - 0.2 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³ | % | 0.1 - 0.2 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Resistivity of conductive plastics | ISO 3915 | Ohm*m | 1E-02 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 330 | |
| Injection molding - Mold temperature | ISO 294 | °C | 85 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1380 |