- Plastics
Makrolon® LED5102
MVR (300 °C/1.2 kg) 34 cm³/10 min; low viscosity; UV stabilized; easy release; high optical transmittance; LED Lighting, optics and lenses
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- พลาสติก
- Transparent, Optical quality
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 260 - 270 | |
| Barrel Temperatures - Middle | - | °C | 250 - 260 | |
| Barrel Temperatures - Nozzle | - | °C | 260 - 270 | |
| Barrel Temperatures - Rear | - | °C | 230 - 240 | |
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 4 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 250 - 300 | |
| Moisture Content max. (%) | - | % | <= 0,02 | |
| Mold Temperatures | - | °C | 70 - 110 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 100 - 200 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 270 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 [UL recognition] | UL 94 | 0.75 mm | Class | V-2 |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.65 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.65 |
| Relative temperature index (Electric strength) | UL 746B | °C | 125 | |
| Relative temperature index (Tensile impact strength) | UL 746B | °C | 115 | |
| Relative temperature index (Tensile strength) | UL 746B | °C | 125 | |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 136 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 123 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 145 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 143 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2350 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 7 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 98 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 73 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 55P |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 12C |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 0 °C/ 3 mm | kJ/m² | 55P |
| Puncture energy | ISO 6603-2 | -30 °C | J | 60 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 55 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 5900 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 4900 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 120 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 60 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2400 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 63 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Haze | ISO 14782 | 1 mm | % | <0.3 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 1 mm | % | 90 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 2 mm | % | 90 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 4 mm | % | 90 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 3 mm | % | 90 |
| Refractive index | ISO 489 | Procedure A | 1.585 | |
| Yellowness index (clear transparent materials) | ASTM E313 | 1 mm | <0.8 | |
| Yellowness index (clear transparent materials) | ASTM E313 | 2 mm | <1 | |
| Yellowness index (clear transparent materials) | ASTM E313 | 3 mm | 1 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt mass-flow rate | ISO 1133 | g/10 min | 37 | |
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 34 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³ | % | 0.7 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³ | % | 0.65 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 280 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1190 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com