- Thermoplastic Polyurethanes
Desmopan 6088A / CQ6088A MBC091
injection molding grade; very good hydrolysis and microbial resistance; easy flowing; low warparge; hard - soft systems
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Thermoplastic Polyurethanes
- Chemical resistant, Scratch resistant, Wear resistant, Tear resistant, Cold-flexibility, Abrasion resistant
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Melt temperature | - | °C | 200 - 220 | |
| Injection molding - Mold temperature | - | °C | 20 - 40 | |
| Maximum drying temperature | - | °C | 100 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Abrasion resistance | ISO 4649 method A | mm³ | 31 | |
| Compression set | DIN ISO 815-1, Method A | 24 h; 70 °C | % | 55 |
| Compression set | DIN ISO 815-1 | 72 h; 23 °C | % | 23 |
| Compression set | DIN ISO 815-1, Method C | 24 h; 70 °C | % | 45 |
| Rebound resilience | ISO 4662 | % | 43 | |
| shore hardness A | DIN ISO 7619-1 | 1s | 88 | |
| Strain at break | DIN 53504 | 200 mm/min | % | 610 |
| Stress at 10 % strain | DIN 53504 | 200 mm/min | MPa | 2,7 |
| Stress at 100 % strain | DIN 53504 | 200 mm/min | MPa | 8,3 |
| Stress at 300 % strain | DIN 53504 | 200 mm/min | MPa | 14 |
| Tear strength | ISO 34-1 | 500 mm/min | kN/m | 46 |
| Ultimate tensile strength | DIN 53504 | 200 mm/min | MPa | 28 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1130 |