- Thermoplastic Polyurethanes
Desmopan 6080A
injection molding grade; free from plasticizers; easy flowing; very good hydrolysis and microbial resistance; low abrasion; automotive interior applications; hard - soft systems; Shoe soles
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Thermoplastic Polyurethanes
- Chemical resistant, Scratch resistant, Wear resistant, Tear resistant, Soft touch, Cold-flexibility, Abrasion resistant
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Melt temperature | - | °C | 200 - 220 | |
| Injection molding - Mold temperature | - | °C | 20 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Tensile storage modulus | ISO 6721-1,-4 | 20 °C | MPa | 21 |
| Tensile storage modulus | ISO 6721-1,-4 | 60 °C | MPa | 13 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Abrasion resistance | ISO 4649 method A | mm³ | 43 | |
| Compression set | DIN ISO 815-1, Method A | 24 h; 70 °C | % | 38 |
| Compression set | DIN ISO 815-1 | 72 h; 23 °C | % | 18 |
| Rebound resilience | ISO 4662 | % | 43 | |
| shore hardness A | DIN ISO 7619-1 | 1s | 80 | |
| Strain at break | DIN 53504 | 200 mm/min | % | 667 |
| Stress at 100 % strain | DIN 53504 | 200 mm/min | MPa | 5,6 |
| Stress at 300 % strain | DIN 53504 | 200 mm/min | MPa | 10,1 |
| Tear strength | ISO 34-1 | 500 mm/min | kN/m | 36 |
| Ultimate tensile strength | DIN 53504 | 200 mm/min | MPa | 28 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1110 |
Downloads
-