Desmopan 3059D DPS 066

injection molding grade; with release agent; excellent abrasion resistance; good wear resistance; Application; Heel patches; Rollers; Boot shells; Injection molded engineering parts

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

No data available

Material

Thermoplastic Polyurethane
Wear resistant, Chemical resistant, Abrasion resistant, Scratch resistant, Tear resistant, Cold-flexibility

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Maximum drying temperature - °C 110
射出成形-溶融温度 - °C 220 - 240
射出成形-金型温度 - °C 20 - 40
Property Name Standard Test condition Unit Value
Tensile storage modulus ISO 6721-1,-4 -20 °C MPa 2435
Tensile storage modulus ISO 6721-1,-4 20 °C MPa 586
Tensile storage modulus ISO 6721-1,-4 60 °C MPa 181
Property Name Standard Test condition Unit Value
Compression set DIN ISO 815-1, Method A 24 h; 70 °C % 42
Compression set DIN ISO 815-1 72 h; 23 °C % 24
Compression set DIN ISO 815-1, Method C 24 h; 70 °C % 31
Rebound resilience ISO 4662 % 35
Tear strength ISO 34-1 500 mm/min kN/m 160
Ultimate tensile strength b.o. ISO 527-1,-3 200 mm/min MPa 65
ショア硬度D DIN ISO 7619-1 1s 58
引張り破断伸び率 b.o. ISO 527-1,-3 200 mm/min % 450
強度 (100%伸び時) b.o. ISO 527-1,-3 200 mm/min MPa 21,8
強度 (300%伸び時) b.o. ISO 527-1,-3 200 mm/min MPa 40
曲げ弾性率 ISO 178 2 mm/min MPa 180 - 180
耐摩耗性 ISO 4649 method A mm³ 18
Property Name Standard Test condition Unit Value
密度 ISO 1183-1 kg/m³ 1230 - 1230

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Do you want to know more about Desmopan 3059D DPS 066?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

1 product to compare