Baypreg® F 200
two-component polyurethane system; very high flexural stiffness and excellent thermal properties; flexural strength 7.5 MPa @ 22°C
i
Market Switch
Selection will influence the results you get.
About
Product Types
- System
Material
No data available
General Characterization
Baypreg F 200 system is a two component polyurethane system used in compression molding.
Storage Conditions
The isocyanate, Component A, is based on diphenylmethane diisocyanate (PMDI). It should be stored in tightly closed containers and protected from moisture and foreign materials, which can adversely affect processing. It will react slowly with water to form ureas and liberate carbon dioxide gas, which may cause sealed containers to expand and rupture. Recommended storage temperatures are 10° to 30°C (50° to 86°F).
The polyol blend, Component B, is hygroscopic and should be protected from atmospheric moisture by sealing the container, or blanketing the product with a dry atmosphere. Contamination with foreign materials, which can adversely affect processing, should be avoided. Materials should be stored at normal room temperature (18° to 30°C). Component B contains pigments which may settle out over time. Initial agitation is recommended before use and after prolonged periods of time
The polyol blend, Component B, is hygroscopic and should be protected from atmospheric moisture by sealing the container, or blanketing the product with a dry atmosphere. Contamination with foreign materials, which can adversely affect processing, should be avoided. Materials should be stored at normal room temperature (18° to 30°C). Component B contains pigments which may settle out over time. Initial agitation is recommended before use and after prolonged periods of time