Baybond® PU 405
Anionic/non-ionic crosslinking polyether urethane polymer.As the film-forming component in glass fibre sizes.
i
Market Switch
Selection will influence the results you get.
About
Product Types
- Dispersion
- Crosslinkers
- Waterbased dispersion
- PU dispersion
- Glass fiber sizing dispersion
Material
No data available
General Characterization
Anionic/non-ionic crosslinking polyether urethane polymer.
As the film-forming component in glass fibre sizes.
As the film-forming component in glass fibre sizes.
Storage Conditions
- Storage in original sealed Covestro container.
- Recommended storage temperature: 5 - 30 °C.
- Protect from frost, heat and foreign material.
General information: The product cannot be used if it has been frozen.
- Recommended storage temperature: 5 - 30 °C.
- Protect from frost, heat and foreign material.
General information: The product cannot be used if it has been frozen.
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Characteristics
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Density at 20 °C | DIN EN ISO 2811/3 | g/ml | approx. 1.04 |
Specifications
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Viscosity at 23°C spindle L1/30 rpm | M092-ISO 2555 | mPa.s | < 200 |
| Particle size Dv 0.9 | µm | ≤ 0.5 | |
| Particle size Dv 0.5 | µm | ≤ 0.3 | |
| pH value 20 °C (supply form) | DIN ISO 976 | 6.0 - 8.0 | |
| Non-volatile content (0.9-1.1g / 1h / 125°C, convection oven) | DIN EN ISO 3251 | % | 32 - 35 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com