- Plastics
Makroblend® KU2-7912/4
(PC+PBT)-blend, impact modified, Injection molding grade, high toughness at low temperatures, ideal for painted applications, unreinforced, applications: automotive body panels
i
Market Switch
Selection will influence the results you get.
About
Product Types
- PC+PBT
Material
- Plastics
- Paintable, Impact resistant, Chemical resistant, Cold stable
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| スクリュー回転数 | - | m/s | 0.1 - 0.2 | |
| バレル温度‐ノズル | - | °C | 260 - 270 | |
| バレル温度‐中部 | - | °C | 240 - 250 | |
| バレル温度‐前部 | - | °C | 250 - 260 | |
| バレル温度‐後部 | - | °C | 230 - 240 | |
| ベント深さ | - | mm | 0.025 - 0.075 | |
| 乾燥時間（除湿乾燥機） | - | h | 2 - 4 | |
| 乾燥温度（除湿乾燥機） | - | °C | 105 | |
| 保圧（最大射出圧比） | - | % | 50 - 75 | |
| 最大含水率 | - | % | <= 0,02 | |
| 最適射出量 (最大射出量比) | - | % | 30 - 70 | |
| 標準樹脂温度 | - | °C | 260 | |
| 樹脂温度 | - | °C | 250 - 270 | |
| 背圧 | - | bar | 50 - 100 | |
| 金型温度 | - | °C | 60 - 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.9 |
| Thermal conductivity, through-plane | ISO 8302 | 23 °C; 50 % r. h. | W/(m*K) | 0.2 |
| グローワイヤーテスト(GWFI) | IEC 60695-2-12 | 2.0 mm | °C | 700 |
| ビカット軟化温度 | ISO 306 | 50 N; 120 °C/h | °C | 120 |
| 燃焼性UL94(1.5mm) | UL 94 | 1.6 mm | Class | HB |
| 燃焼試験(US-FMVSS) | ISO 3795 | >=1.0 mm | mm/min | passed |
| 線膨張係数、流動方向 | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.9 |
| 荷重たわみ温度 | ISO 75-1,-2 | 0.45 MPa | °C | 106 |
| 荷重たわみ温度 | ISO 75-1,-2 | 1.80 MPa | °C | 82 |
| 融点 | ISO 11357-1,-3 | 10 °C/min | °C | 223 |
| 酸素指数 | ISO 4589-2 | Method A | % | 21 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| アイゾット衝撃強度 | ISO 180/U | -30 °C | kJ/m² | N |
| アイゾット衝撃強度 | ISO 180/U | 23 °C | kJ/m² | N |
| シャルピー衝撃強度 | ISO 179/1eU | -30 °C | kJ/m² | N |
| シャルピー衝撃強度 | ISO 179/1eU | 23 °C | kJ/m² | N |
| ノッチ付き アイゾット衝撃強度 | ISO 180/A | 23 °C | kJ/m² | 60 |
| ノッチ付き アイゾット衝撃強度 | ISO 180/A | -20 °C | kJ/m² | 52 |
| ノッチ付き アイゾット衝撃強度 | ISO 180/A | -30 °C | kJ/m² | 45 |
| ノッチ付き シャルピー衝撃強度 | ISO 179/1eA | -30 °C | kJ/m² | 45 |
| ノッチ付き シャルピー衝撃強度 | ISO 179/1eA | 23 °C | kJ/m² | 60 |
| 圧球式硬度 | ISO 2039-1 | N/mm² | 100 | |
| 引張り弾性率 | ISO 527-1,-2 | 1 mm/min | MPa | 2050 |
| 引張り破断伸び率 | ISO 527-1,-2 | 50 mm/min | % | > 50 |
| 引張り破断強度 | ISO 527-1,-2 | 50 mm/min | MPa | 45 |
| 引張り降伏伸び率 | ISO 527-1,-2 | 50 mm/min | % | 4 |
| 引張り降伏応力 | ISO 527-1,-2 | 50 mm/min | MPa | 50 |
| 曲げ強度 | ISO 178 | 2 mm/min | MPa | 75 |
| 曲げ弾性率 | ISO 178 | 2 mm/min | MPa | 2100 |
| 曲げ応力 （3.5%歪み時） | ISO 178 | 2 mm/min | MPa | 66 |
| 曲げ歪み （曲げ強度時） | ISO 178 | 2 mm/min | % | 5.5 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Göttfert 溶融粘度 | Bayer test | 165 s^-1^/ 260 °C | Pa*s | 670 |
| MVR | ISO 1133 | 260 °C/ 5 kg | cm³/10 min | 16 |
| 後収縮、 流動方向/垂直方向 | b.o. ISO 2577 | Value range based on general practical experience (1h; 90°C) | % | 0.1 - 0.2 |
| 成形収縮率、流動方向/垂直方向 | b.o. ISO 2577 | Value range based on general practical experience (600bar) | % | 0.7 - 0.9 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| 体積抵抗率 | IEC 62631-3-1 | Ohm*m | >1E15 | |
| 比誘電率 | IEC 60250 | 1 MHz | 3.1 | |
| 比誘電率 | IEC 60250 | 100 Hz | 3.2 | |
| 絶縁破壊強度 | IEC 60243-1 | 1 mm | kV/mm | 35 |
| 耐トラッキングﾞ性 CTI | IEC 60112 | Solution A | Rating | 500 |
| 耐トラッキングﾞ性 CTI M | IEC 60112 | Solution B | Rating | 100 |
| 表面抵抗率 | IEC 62631-3-2 | Ohm | >1E17 | |
| 誘電正接 | IEC 60250 | 1 MHz | 10^-4^ | 130 |
| 誘電正接 | IEC 60250 | 100 Hz | 10^-4^ | 15 |
| 電食性 | IEC 60426 | Rating | A1 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| 射出成形-射出速度 | ISO 294 | mm/s | 200 | |
| 射出成形-溶融温度 | ISO 294 | °C | 260 | |
| 射出成形-金型温度 | ISO 294 | °C | 70 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| かさ密度 | ISO 60 | g/cm³ | 0.7 | |
| 吸水率 （平衡) | ISO 62 | 23 °C; 50 % r. h. | % | 0.2 |
| 吸水率 （飽和) | ISO 62 | Water at 23 °C | % | 0.6 |
| 密度 | ISO 1183-1 | kg/m³ | 1200 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com
-
Viskosität Schergeschwindigkeit Makroblend® KU2-7912/4 (Multipoint Data Sheet) Viscosity Shear Rate Makroblend® KU2-7912/4 (Multipoint Data Sheet)
-
Secant modulus - Strain Makroblend® KU2-7912/4 (Multipoint Data Sheet) Sekantenmodul-Dehnung Makroblend® KU2-7912/4 (Multipoint Data Sheet)
-
Spannung-Dehnung Makroblend® KU2-7912/4 (Multipoint Data Sheet) Stress-Strain Makroblend® KU2-7912/4 (Multipoint Data Sheet)
-
Specific Volume-Temperature (pvT) Makroblend® KU2-7912/4 (Multipoint Data Sheet) Spezifisches Volumen-Temperatur (pvT) Makroblend® KU2-7912/4 (Multipoint Data Sheet)