Bayblend® M850 XF
(PC+ABS)-Blend; easy flowing; Vicat/B 120 temperature = 131 °C; meet certain requirements of ISO Standard 10993-1; for further information please contact plastics@covestro.com
i
Market Switch
Selection will influence the results you get.
About
Product Types
- PC+ABS blend
Material
- Plastics
- Medical
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Barrel Temperatures - Front | - | °C | 240 - 270 | |
Barrel Temperatures - Middle | - | °C | 235 - 245 | |
Barrel Temperatures - Nozzle | - | °C | 265 - 275 | |
Barrel Temperatures - Rear | - | °C | 230 - 240 | |
Dry Air Drying Temperature | - | °C | 95 - 110 | |
Dry Air Drying Time | - | h | 4 | |
Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
Melt temperatures | - | °C | 260 - 280 | |
Moisture Content max. (%) | - | % | <= 0,02 | |
Mold Temperatures | - | °C | 70 - 90 | |
Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
Shot-to-Cylinder Size | - | % | 30 - 70 | |
Standard Melt temperature | - | °C | 270 | |
Vent Depth | - | mm | 0.025 - 0.075 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Burning behavior UL 94 [UL recognition] | UL 94 | 0.85 mm | Class | HB |
Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 127 |
Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 109 |
Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 131 |
Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 129 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Izod impact strength | ISO 180/U | 23 °C | kJ/m² | N |
Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 48 |
Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 15 |
Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | > 50 |
Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 53 |
Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2500 |
Yield strain | ISO 527-1,-2 | 50 mm/min | % | 4.9 |
Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 62 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 260 °C | Pa*s | 210 |
Melt volume-flow rate | ISO 1133 | 260 °C/ 5 kg | cm³/10 min | 25 |
Molding shrinkage, normal | b.o. ISO 2577 | 150x105x3 mm³/ 260 °C / MT 80 °C | % | 0.55 - 0.75 |
Molding shrinkage, parallel | b.o. ISO 2577 | 150x105x3 mm³/ 260 °C / MT 80 °C | % | 0.55 - 0.75 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 250 |
Dissipation factor | IEC 60250 | 1 MHz | 10^-4^ | 90 |
Dissipation factor | IEC 60250 | 100 Hz | 10^-4^ | 30 |
Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 35 |
Relative permittivity | IEC 60250 | 1 MHz | 2.9 | |
Relative permittivity | IEC 60250 | 100 Hz | 2.9 | |
Surface resistivity | IEC 62631-3-2 | Ohm | 1E17 | |
Volume resistivity | IEC 62631-3-1 | Ohm*m | 1E14 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Injection molding - Injection velocity | ISO 294 | mm/s | 240 | |
Injection molding - Melt temperature | ISO 294 | °C | 260 | |
Injection molding - Mold temperature | ISO 294 | °C | 80 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Density | ISO 1183-1 | kg/m³ | 1140 | |
Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.2 |
Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.7 |