Makrolon® M6011 FR
medium viscosity; impact modified; UV stabilized; flame retardant; improved chemical resistance compared to standard Makrolon grades; tested only according to ISO 10993-5 and ISO 10993-10 for contact with uncompromised skin only; electrical/electronic; housing parts
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- Medical, Flame retardant
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 4 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 | UL 94 | 1.0 mm | Class | V-1 |
| Burning behavior UL 94 | UL 94 | 1.5 mm | Class | V-0 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.0 mm | °C | 960 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 960 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 1.0 mm | °C | 875 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 1.5 mm | °C | 850 |
| Resistance to heat (ball pressure test) | IEC 60695-10-2 | °C | 125 | |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 129 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 115 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 138 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 136 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2250 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 89 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 70 P |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 20 C |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | >50 |
| Puncture energy | ISO 6603-2 | -30 °C | J | 57 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 51 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 6200 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5000 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2250 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 5.9 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 60 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C | Pa*s | 320 |
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 4 |
| Melt volume-flow rate | ISO 1133 | 300 °C/ 5 kg | cm³/10 min | 25 |
| Molding shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience | % | 0.6 - 0.8 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Melt temperature | ISO 294 | °C | 300 | |
| Injection molding - Mold temperature | ISO 294 | °C | 90 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1190 | |
| Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.12 |
| Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.36 |