Makrolon® FR6002

MVR (300 °C/1.2 kg) 18 cm³/10 min; flame retardant; low viscosity; easy release

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • Polycarbonate

Material

Plastics
Transparent, Flame retardant

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 280 - 290
Barrel Temperatures - Middle - °C 270 - 280
Barrel Temperatures - Nozzle - °C 290 - 300
Barrel Temperatures - Rear - °C 250 - 260
Dry Air Drying Temperature - °C 120
Dry Air Drying Time - h 2 - 3
Hold Pressure (% of injection pressure) - % 50 - 75
Melt temperatures - °C 280 - 320
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 80 - 120
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt temperature - °C 300
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 [UL recognition] UL 94 1.5 mm Class V-0 (WT, GY, BK)
Burning behavior UL 94 [UL recognition] UL 94 0.75 mm Class V-0 (WT, GY, BK)
Burning behavior UL 94 [UL recognition] UL 94 3.0 mm Class V-0 (WT, GY, BK)
Glow wire test (GWFI) IEC 60695-2-12 0.75 mm °C 960
Glow wire test (GWFI) IEC 60695-2-12 1.5 mm °C 960
Glow wire test (GWFI) IEC 60695-2-12 3.0 mm °C 960
Glow wire test (GWIT) IEC 60695-2-13 0.75 mm °C 850
Glow wire test (GWIT) IEC 60695-2-13 1.5 mm °C 850
Glow wire test (GWIT) IEC 60695-2-13 3.0 mm °C 930
Oxygen index ISO 4589-2 Method A % > 32
Relative temperature index (Electric strength) UL 746B 1.5 mm °C 120
Relative temperature index (Tensile impact strength) UL 746B 1.5 mm °C 110
Relative temperature index (Tensile strength) UL 746B 1.5 mm °C 120
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 137
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 124
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 143
Property Name Standard Test condition Unit Value
Charpy impact strength ISO 179/1eU 23 °C kJ/m² N
Izod notched impact strength ISO 21305/based on ISO 180/A 23 °C/ 3 mm kJ/m² 15P(C)
Nominal strain at break ISO 527-1,-2 50 mm/min % > 50
Strain at break b.o. ISO 527-1,-2 50 mm/min % 120
Stress at break ISO 527-1,-2 50 mm/min MPa 65
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2350
Yield strain ISO 527-1,-2 50 mm/min % 6
Yield stress ISO 527-1,-2 50 mm/min MPa 64
Property Name Standard Test condition Unit Value
Melt volume-flow rate ISO 1133 300 °C/ 1.2 kg cm³/10 min 18
Molding shrinkage, parallel/normal b.o. ISO 2577 Value range based on general practical experience % 0.5 - 0.7
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 250-<1
Comparative tracking index CTI M IEC 60112 Solution B Rating 125 M-<1
Dissipation factor IEC 60250 1 MHz 10^-4^ 88
Dissipation factor IEC 60250 100 Hz 10^-4^ 8
Electrical strength IEC 60243-1 1 mm kV/mm 34
Relative permittivity IEC 60250 1 MHz 2,9
Relative permittivity IEC 60250 100 Hz 3
Surface resistivity IEC 60093 Ohm 4,2E16
Volume resistivity IEC 60093 Ohm*m 1,5E15
Property Name Standard Test condition Unit Value
Injection molding - Injection velocity ISO 294 mm/s 200
Injection molding - Melt temperature ISO 294 °C 280
Injection molding - Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1200

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com

Do you want to know more about Makrolon® FR6002?
Get in touch with our experts!

Contact form image Zoe

How would you describe yourself?

What type of material are you interested in?

What type of inquiry is this?

How can we contact you?

* Mandatory Fields

Compare