Makroblend® UT305 RE CQ
(PC+PET) blend; easy-flow; injection molding Grade; high heat resistance; good chemical resistance; good flowability; good surface appearance and exceptional dimensional stability, even in high moisture environments
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- CQ renewable attributed
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 255 - 265 | |
| Barrel Temperatures - Middle | - | °C | 250 - 260 | |
| Barrel Temperatures - Nozzle | - | °C | 255 - 270 | |
| Barrel Temperatures - Rear | - | °C | 245 - 255 | |
| Dry Air Drying Temperature | - | °C | 110 | |
| Dry Air Drying Time | - | h | 2 - 4 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 260 - 280 | |
| Moisture Content max. (%) | - | % | <= 0,01 | |
| Mold Temperatures | - | °C | 50 - 100 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 270 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 (1.5 mm) [UL recognition] | UL 94 | 1.5 mm | Class | HB |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
| Relative temperature index (Electric strength) [UL recognition] | UL 746B | °C | 75 | |
| Relative temperature index (Tensile impact strength) [UL recognition] | UL 746B | °C | 75 | |
| Relative temperature index (Tensile strength) [UL recognition] | UL 746B | °C | 75 | |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 128 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 109 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 139 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | -30 °C | kJ/m² | N |
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Charpy notched impact strength | ISO 179/1eA | -30 °C | kJ/m² | 6 |
| Charpy notched impact strength | ISO 179/1eA | 23 °C | kJ/m² | 8 |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2600 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 6.2 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 100 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 80 |
| Izod impact strength | ISO 180/1C | -30 °C | kJ/m² | >180P |
| Izod impact strength | ISO 180/U | -30 °C | kJ/m² | N |
| Izod impact strength | ISO 180/1C | 23 °C | kJ/m² | >180P |
| Izod impact strength | ISO 180/U | 23 °C | kJ/m² | N |
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 8 |
| Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 8 |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | 100 |
| Puncture energy | ISO 6603-2 | -30 °C | J | 62 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 54 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 5800 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 4600 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 120 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 69 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2600 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 5.4 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 69 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^ | Pa*s | 210 |
| Melt volume-flow rate | ISO 1133 | 270 °C/ 5 kg | cm³/10 min | 39 |
| Molding shrinkage, normal | b.o. ISO 2577 | 150x105x3 mm³/ 270 °C / MT 70°C | % | 0.6 - 0.8 |
| Molding shrinkage, parallel | b.o. ISO 2577 | 150x105x3 mm³/ 270 °C / MT 70°C | % | 0.6 - 0.8 |
| Post- shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience (1h; 90°C) | % | 0.01-0.1 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 270 | |
| Injection molding - Mold temperature | ISO 294 | °C | 70 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1240 | |
| Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.25 |
| Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.55 |