Makroblend® M5005 FR RE CQ
(PC+PBT) blend; impact modified; flame-retardant; dimensional stability and excellent chemical resistance; good impact strength; injection molding Grade; Tested only according to ISO 10993-5 and ISO 10993-10 for contact with uncompromised skin only; manufactured according to GMP
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- Medical, CQ renewable attributed
- Foams
- Flame retardant
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Dry Air Drying Temperature | - | °C | 80 | |
| Dry Air Drying Time | - | h | 4 - 6 | |
| Moisture Content max. (%) | - | % | <0.02 | |
| Mold Temperatures | - | °C | 70 | |
| Standard Melt temperature | - | °C | 260 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 [UL recognition] | UL 94 | 2.4 mm | Class | V-0 |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.9 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.9 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 90 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 78 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 99 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2350 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 85 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 75 |
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 45 |
| Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 12 |
| Nominal strain at break | ISO 527-1,-2 | 5 mm/min | % | 130 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 50 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 3750 |
| Stress at break | ISO 527-1,-2 | 5 mm/min | MPa | 55 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2300 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 4 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 55 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 260 °C | Pa*s | 260 |
| Melt volume-flow rate | ISO 1133 | 260 °C/ 5 kg | cm³/10 min | 32 |
| Molding shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience (600bar) | % | 0.6 - 0.8 |
| Post- shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience (1h; 90°C) | % | 0.6-0.8 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1240 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com