Desmopan 85085A DPS 055
injection molding grade; no yellowing under the action of UV light; improved microbial resistance; good low-temperature flexibility; Improved hydrolysis resistance; Application; automotive interior applications
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Maximum drying temperature | - | °C | 80 | |
| 射出成形-溶融温度 | - | °C | 180 - 210 | |
| 射出成形-金型温度 | - | °C | 20 - 40 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Tensile storage modulus | ISO 6721-1,-4 | -20 °C | MPa | 207 |
| Tensile storage modulus | ISO 6721-1,-4 | 20 °C | MPa | 86 |
| Tensile storage modulus | ISO 6721-1,-4 | 60 °C | MPa | 55 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Compression set | DIN ISO 815-1, Method A | 24 h; 70 °C | % | 40 |
| Compression set | DIN ISO 815-1 | 72 h; 23 °C | % | 18 |
| Compression set | DIN ISO 815-1, Method C | 24 h; 70 °C | % | 23 |
| Rebound resilience | ISO 4662 | % | 63 | |
| Tear strength | ISO 34-1 | 500 mm/min | kN/m | 75 |
| Ultimate tensile strength | DIN 53504 | 200 mm/min | MPa | 31.3 |
| ショア硬度A | DIN ISO 7619-1 | 1s | 85 | |
| 引張り破断伸び率 | DIN 53504 | 200 mm/min | % | 823 |
| 強度 （10%伸び時） | DIN 53504 | 200 mm/min | MPa | 2,4 |
| 強度 （100%伸び時） | DIN 53504 | 200 mm/min | MPa | 6,4 |
| 強度 （300%伸び時） | DIN 53504 | 200 mm/min | MPa | 10,7 |
| 強度 （50%伸び時） | DIN 53504 | 200 mm/min | MPa | 5,1 |
| 耐摩耗性 | ISO 4649 method A | mm³ | 28 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| 密度 | ISO 1183-1 | kg/m³ | 1130 |