Makrolon® FR6020
polycarbonate; medium viscosity; easy release; UV stabilized; flame retardant; non-reinforced; good hydrolysis resistance; impact modified; Information technology; electrical/electronic
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 | UL 94 | 2.0 mm | Class | V-0 |
| Burning behavior UL 94 (1.5 mm) | UL 94 | Class | V-0 | |
| Burning behavior UL 94-5V | UL 94 | 2.0 mm | Class | 5VB |
| Burning behavior UL 94-5V | UL 94 | 3.0 mm | Class | 5VA |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.58 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.49 |
| Relative temperature index (Electric strength) | UL 746B | 1.5 mm | °C | 125 |
| Relative temperature index (Tensile impact strength) | UL 746B | 1.5 mm | °C | 115 |
| Relative temperature index (Tensile strength) | UL 746B | 1.5 mm | °C | 125 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 127 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 114 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 136 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 134 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | 23 °C | kJ/m² | 69P |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | -30 °C | kJ/m² | 33C |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | -20 °C | kJ/m² | 56C |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2430 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 6 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 90 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 74 |
| Izod impact strength | ISO 180/U | -30 °C | kJ/m² | N |
| Izod impact strength | ISO 180/U | 23 °C | kJ/m² | N |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C | kJ/m² | 67P |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | > 100 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 58 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2380 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 58 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C | Pa*s | 260 |
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 9 |
| Molding shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience | % | 0.6 - 0.8 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Melt temperature | ISO 294 | °C | 280 - 300 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1200 |