- Plastics
Makrolon® TC210 RE CQ
moderate thermal conductivity; MVR (300 °C/1.2 kg) 4.0 cm³/10 min; high viscosity; electrically insulating; components for heat dissipation
i
Market Switch
Selection will influence the results you get.
About
Product Types
- Polycarbonate
Material
- Plastics
- CQ renewable attributed, Thermal conductive
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 270 - 290 | |
| Barrel Temperatures - Middle | - | °C | 260 - 280 | |
| Barrel Temperatures - Nozzle | - | °C | 280 - 300 | |
| Barrel Temperatures - Rear | - | °C | 250 - 270 | |
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 4 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 290 | |
| Moisture Content max. (%) | - | % | <0.2 | |
| Mold Temperatures | - | °C | 80 - 90 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Vent Depth | - | mm | 0.0025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 | UL 94 | 1.0 mm | Class | HB (Covestro Test) |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.5 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.3 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 850 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 1.5 mm | °C | 850 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 144 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 136 |
| Thermal conductivity, in-plane | ASTM E1461 | 23 °C; 50 % r. h. | W/(m*K) | 1.4 |
| Thermal conductivity, through-plane | ASTM E1461 | 23 °C; 50 % r. h. | W/(m*K) | 0.3 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 146 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Ball indentation hardness | ISO 2039-1 | N/mm² | 128 | |
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | 12 |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 8700 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 1.5 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 80 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 0 |
| Nominal strain at break | ISO 527-1,-2 | 5 mm/min | % | 1.4 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 3 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 600 |
| Stress at break | ISO 527-1,-2 | 5 mm/min | MPa | 49 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 7800 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C | Pa*s | 180 |
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 280 °C | Pa*s | 300 |
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 4 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³ | % | 0.3 - 0.4 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 40 |
| Surface resistivity | IEC 62631-3-2 | Ohm | >=1E+16 | |
| Volume resistivity | IEC 62631-3-1 | Ohm*m | >=1E+16 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Melt temperature | ISO 294 | °C | 280 | |
| Injection molding - Mold temperature | ISO 294 | °C | 90 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1560 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com