Makrolon® FR6005 RE
polycarbonate; MVR (300 °C/1.2 kg) 9.0 cm³/10 min; medium viscosity; easy release; flame retardant; impact modified; good surface quality; electrical/electronic; housing parts
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- Impact resistant, CQ renewable attributed
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 280 - 290 | |
| Barrel Temperatures - Middle | - | °C | 270 - 280 | |
| Barrel Temperatures - Nozzle | - | °C | 290 - 300 | |
| Barrel Temperatures - Rear | - | °C | 250 - 260 | |
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 2 - 3 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 280 - 320 | |
| Moisture Content max. (%) | - | % | <= 0.02 | |
| Mold Temperatures | - | °C | 80 - 120 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 300 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 | UL 94 | 1.2 mm (BK) | Class | V-0 |
| Burning behavior UL 94 [UL recognition] | UL 94 | 1.5 mm | Class | V-0 |
| Burning behavior UL 94 [UL recognition] | UL 94 | 1.0 mm (BK) | Class | V-0 |
| Burning behavior UL 94 [UL recognition] | UL 94 | 3.0 mm | Class | V-0 |
| Burning behavior UL 94 [UL recognition] | UL 94 | 1.2 mm | Class | V-1 |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.0 mm | °C | 850 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 960 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 960 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 1.0 mm | °C | 875 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 1.5 mm | °C | 850 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 3.0 mm | °C | 900 |
| Relative temperature index (Electric strength) | UL 746B | 0.75 mm | °C | 115 |
| Relative temperature index (Tensile impact strength) | UL 746B | 0.75 mm | °C | 105 |
| Relative temperature index (Tensile strength) | UL 746B | 0.75 mm | °C | 115 |
| Resistance to heat (ball pressure test) | IEC 60695-10-2 | °C | 134 | |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 136 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 121 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 144 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 142 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | 23 °C | kJ/m² | 68P |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | -10 °C | kJ/m² | 50C |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | -30 °C | kJ/m² | 20C |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2400 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 90 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 60P |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 15C |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | > 50 |
| Puncture energy | ISO 6603-2 | -30 °C | J | 55 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 54 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 6100 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5100 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 135 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 66 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2300 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 62 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 9 |
| Molding shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience | % | 0.6 - 0.8 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 200 |
| Surface resistivity | IEC 62631-3-2 | Ohm | 4E17 | |
| Volume resistivity | IEC 62631-3-1 | Ohm*m | 9E16 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 300 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1200 |