Makrolon® 3207 MAS403
MVR (300 °C/1.2 kg) 4.0 cm³/10 min; general purpose; high viscosity; UV stabilized; easy release; developed for safety goggles
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Barrel Temperatures - Front | - | °C | 290 - 300 | |
Barrel Temperatures - Middle | - | °C | 280 - 290 | |
Barrel Temperatures - Nozzle | - | °C | 300 - 310 | |
Barrel Temperatures - Rear | - | °C | 260 - 270 | |
Dry Air Drying Temperature | - | °C | 120 | |
Dry Air Drying Time | - | h | 2 - 3 | |
Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
Melt temperatures | - | °C | 290 - 330 | |
Moisture Content max. (%) | - | % | <= 0,02 | |
Mold Temperatures | - | °C | 80 - 120 | |
Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
Shot-to-Cylinder Size | - | % | 30 - 70 | |
Standard Melt temperature | - | °C | 310 | |
Vent Depth | - | mm | 0.025 - 0.075 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Glass transition temperature | ISO 11357-1,-2 | 10 °C/min | °C | 150 |
Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 141 |
Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 127 |
Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 146 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Charpy impact strength | ISO 179/1eU | -60 °C | kJ/m² | N |
Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 6.8 |
Flexural strength | ISO 178 | 2 mm/min | MPa | 96 |
Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 74 |
Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 80P |
Izod notched impact strength | ISO 21305/based on ISO 180/A | -20 °C/ 3 mm | kJ/m² | 70P(C) |
Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 20C(P) |
Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | > 50 |
Puncture energy | ISO 6603-2 | 23 °C | J | 65 |
Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5900 |
Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 120 |
Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2400 |
Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6.5 |
Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 65 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Haze for transparent materials | ISO 14782 | 3 mm | % | 0.4 |
Luminous transmittance (clear transparent materials) | ISO 13468-2 | 1 mm | % | 89 |
Luminous transmittance (clear transparent materials) | ISO 13468-2 | 2 mm | % | 88 |
Luminous transmittance (clear transparent materials) | ISO 13468-2 | 4 mm | % | 87 |
Luminous transmittance (clear transparent materials) | ISO 13468-2 | 3 mm | % | 88 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 4 |
Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³ | % | 0.75 |
Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³ | % | 0.7 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
Injection molding - Melt temperature | ISO 294 | °C | 310 | |
Injection molding - Mold temperature | ISO 294 | °C | 90 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Density | ISO 1183-1 | kg/m³ | 1190 |