Makrolon® 3207 MAS403 RE
MVR (300 °C/1.2 kg) 4.0 cm³/10 min; general purpose; high viscosity; UV stabilized; easy release; developed for safety goggles
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- CQ renewable attributed
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 290 - 300 | |
| Barrel Temperatures - Middle | - | °C | 280 - 290 | |
| Barrel Temperatures - Nozzle | - | °C | 300 - 310 | |
| Barrel Temperatures - Rear | - | °C | 260 - 270 | |
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 2 - 3 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 290 - 330 | |
| Moisture Content max. (%) | - | % | <= 0,02 | |
| Mold Temperatures | - | °C | 80 - 120 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 310 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Glass transition temperature | ISO 11357-1,-2 | 10 °C/min | °C | 150 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 141 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 127 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 146 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | -60 °C | kJ/m² | N |
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 6.8 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 96 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 74 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 80P |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -20 °C/ 3 mm | kJ/m² | 70P(C) |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 20C(P) |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | > 50 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 65 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5900 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 120 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2400 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6.5 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 65 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Haze for transparent materials | ISO 14782 | 3 mm | % | 0.4 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 1 mm | % | 89 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 2 mm | % | 88 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 4 mm | % | 87 |
| Luminous transmittance (clear transparent materials) | ISO 13468-2 | 3 mm | % | 88 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 4 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³ | % | 0.75 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³ | % | 0.7 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 310 | |
| Injection molding - Mold temperature | ISO 294 | °C | 90 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1190 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com