Makrolon® 2405 XT
polycarbonate; MVR (300 °C/1.2 kg) 19 cm³/10 min; Automotive lighting; low viscosity; easy release; extreme high processing temperature resistance for thin-walled 1K and 2K applications; automotive lenses and bezels
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 310 - 320 | |
| Barrel Temperatures - Middle | - | °C | 300 - 310 | |
| Barrel Temperatures - Nozzle | - | °C | 320 - 330 | |
| Barrel Temperatures - Rear | - | °C | 280 - 290 | |
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 2 - 3 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 280 - 350 | |
| Moisture Content max. (%) | - | % | <= 0.02 | |
| Mold Temperatures | - | °C | 80 - 120 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 330 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.65 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.65 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 137 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 125 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 146 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 145 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Ball indentation hardness | ISO 2039-1 | N/mm² | 115 | |
| Charpy impact strength | ISO 179/1eU | -30 °C | kJ/m² | N |
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2350 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 7 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 97 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 73 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 60P |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 12C |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | > 50 |
| Puncture energy | ISO 6603-2 | -30 °C | J | 65 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 55 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 6000 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5100 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 120 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 65 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2400 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 65 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 19 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³/ 500 bar | % | 0.65 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³/ 500 bar | % | 0.65 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1200 |