Makroblend® UT403
(PC+PET) blend, unreinforced; UV-stabilized; impact modified; high flow; injection molding grade. Good impact strength, dimensional stability and chemical resistance. UL746C f1 rated.
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- Chemical resistant, UV stable, Heat resistant, Impact resistant
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Barrel Temperatures - Front | - | °C | 255 - 265 | |
Barrel Temperatures - Middle | - | °C | 250 - 260 | |
Barrel Temperatures - Nozzle | - | °C | 255 - 270 | |
Barrel Temperatures - Rear | - | °C | 245 - 255 | |
Dry Air Drying Temperature | - | °C | 110 | |
Dry Air Drying Time | - | h | 2 - 4 | |
Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
Melt temperatures | - | °C | 260 - 280 | |
Moisture Content max. (%) | - | % | <= 0,01 | |
Mold Temperatures | - | °C | 50 - 100 | |
Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
Shot-to-Cylinder Size | - | % | 30 - 70 | |
Standard Melt temperature | - | °C | 270 | |
Vent Depth | - | mm | 0.025 - 0.075 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Burning behavior UL 94 (1.5 mm) [UL recognition] | UL 94 | Class | HB | |
Burning behavior UL 94 [UL recognition] | UL 94 | 3.0 mm | Class | HB |
Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.8 |
Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 124 |
Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 98 |
Thermal conductivity, through-plane | ISO 8302 | 23 °C; 50 % r. h. | W/(m*K) | 0.2 |
Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 139 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Flexural modulus | ISO 178 | 2 mm/min | MPa | 2300 |
Flexural strength | ISO 178 | 2 mm/min | MPa | 86 |
Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 72 |
Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 70 |
Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 20 |
Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | 100 |
Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 58 |
Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2400 |
Yield strain | ISO 527-1,-2 | 50 mm/min | % | 5 |
Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 58 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Melt volume-flow rate | ISO 1133 | 270 °C/ 5 kg | cm³/10 min | 34 |
Molding shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience (600bar) | % | 0.6 - 0.8 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 200 |
Dissipation factor | IEC 60250 | 1 MHz | 10^-4^ | 150 |
Dissipation factor | IEC 60250 | 100 Hz | 10^-4^ | 17 |
Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 34 |
Relative permittivity | IEC 60250 | 1 MHz | 3.1 | |
Relative permittivity | IEC 60250 | 100 Hz | 3.2 | |
Surface resistivity | IEC 62631-3-2 | Ohm | 1E16 | |
Volume resistivity | IEC 62631-3-1 | Ohm*m | 1E14 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
Injection molding - Melt temperature | ISO 294 | °C | 270 | |
Injection molding - Mold temperature | ISO 294 | °C | 70 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Density | ISO 1183-1 | kg/m³ | 1230 | |
Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.2 |
Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.5 |