Bayblend® T90 XG RE25 CQ
(PC+ABS)-Blend; Vicat/B 120 temperature = 135 °C; easy flowing; optimized surface quality for metallization (steam treatment)
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Barrel Temperatures - Front | - | °C | 240 - 270 | |
Barrel Temperatures - Middle | - | °C | 235 - 245 | |
Barrel Temperatures - Nozzle | - | °C | 265 - 275 | |
Barrel Temperatures - Rear | - | °C | 230 - 240 | |
Dry Air Drying Temperature | - | °C | 95 - 110 | |
Dry Air Drying Time | - | h | 4 | |
Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
Melt temperatures | - | °C | 260 - 280 | |
Moisture Content max. (%) | - | % | <= 0.02 | |
Mold Temperatures | - | °C | 70 - 90 | |
Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
Shot-to-Cylinder Size | - | % | 30 - 70 | |
Standard Melt temperature | - | °C | 270 | |
Vent Depth | - | mm | 0.025 - 0.075 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 130 |
Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 112 |
Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 135 |
Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 134 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Izod impact strength | ISO 180/U | 23 °C | kJ/m² | N |
Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 52 |
Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 18 |
Puncture energy | ISO 6603-2 | -30 °C | J | 57 |
Puncture energy | ISO 6603-2 | 23 °C | J | 51 |
Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | > 50 |
Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 56 |
Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2400 |
Yield strain | ISO 527-1,-2 | 50 mm/min | % | 5.1 |
Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 61 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 260 °C | Pa*s | 225 |
Melt volume-flow rate | ISO 1133 | 260 °C/ 5 kg | cm³/10 min | 26 |
Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³/ 260 °C / MT 80 °C | % | 0.55 - 0.75 |
Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³/ 260 °C / MT 80 °C | % | 0.55 - 0.75 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Dissipation factor | IEC 60250 | 1 MHz | 10^-4^ | 100 |
Dissipation factor | IEC 60250 | 100 Hz | 10^-4^ | 25 |
Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 35 |
Relative permittivity | IEC 60250 | 1 MHz | 3.0 | |
Relative permittivity | IEC 60250 | 100 Hz | 3.1 | |
Surface resistivity | IEC 62631-3-2 | Ohm | 1E16 | |
Volume resistivity | IEC 62631-3-1 | Ohm*m | 1E14 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Injection molding - Injection velocity | ISO 294 | mm/s | 240 | |
Injection molding - Melt temperature | ISO 294 | °C | 260 | |
Injection molding - Mold temperature | ISO 294 | °C | 80 |
Property Name | Standard | Test condition | Unit | Value |
---|---|---|---|---|
Density | ISO 1183-1 | kg/m³ | 1150 | |
Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.2 |
Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.5 |