Bayblend® FR3021 R30
Polycarbonate, impact modified with ABS; 15 % mineral filled; with 30 % post consumer recyclate; Vicat/B 120 temperature = 98 °C; medium viscosity; medium modulus; low warpage; flame-retardant;
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- CQ mechanical recycled
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 240 - 260 | |
| Barrel Temperatures - Middle | - | °C | 230 - 245 | |
| Barrel Temperatures - Nozzle | - | °C | 240 - 265 | |
| Barrel Temperatures - Rear | - | °C | 220 - 235 | |
| Dry Air Drying Temperature | - | °C | 85 | |
| Dry Air Drying Time | - | h | 4 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 230 - 270 | |
| Moisture Content max. (%) | - | % | 0.02 | |
| Mold Temperatures | - | °C | 60 - 80 | |
| Peripheral Screw Speed | - | m/s | 0.1 - 0.3 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 100 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 240 | |
| Vent Depth | - | mm | 0.02 - 0.04 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 | UL 94 | 1.2 mm | Class | V-0 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 92 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 86 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 98 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 95 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Ball indentation hardness | ISO 2039-1 | New | N/mm² | 134 |
| Charpy impact strength | ISO 179/1eU | -30 °C | kJ/m² | 84 |
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | 106 |
| Charpy notched impact strength | ISO 179/1eA | -30 °C | kJ/m² | 5 |
| Charpy notched impact strength | ISO 179/1eA | 23 °C | kJ/m² | 6 |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 4600 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 4.3 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 103 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 101 |
| Izod impact strength | ISO 180/U | -30 °C | kJ/m² | 68 |
| Izod impact strength | ISO 180/U | 23 °C | kJ/m² | 78 |
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 6 |
| Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 5 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 36 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 4000 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 8.6 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 40 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 4700 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 2.8 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 63 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 260 °C | Pa*s | 205 |
| Melt volume-flow rate | ISO 1133 | 240 °C/ 5 kg | cm³/10 min | 12 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³/ 260 °C / MT 80 °C/ 500 bar | % | 0.27 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³/ 260 °C / MT 80 °C/ 500 bar | % | 0.28 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 240 | |
| Injection molding - Melt temperature | ISO 294 | °C | 240 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1310 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com