Bayblend® FR3020 R35 CQ
(PC+ABS)-Blend; flame retardant; contains 35% post consumer PC recyclate for natural color; 5 % mineral filled; medium viscosity; Housing; for: information technology; Electrical/electronic
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- CQ mechanical recycled
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Dry Air Drying Temperature | - | °C | 80 | |
| Dry Air Drying Time | - | h | 4 | |
| Melt temperatures | - | °C | 240 - 270 | |
| Moisture Content max. (%) | - | % | 0.02 | |
| Mold Temperatures | - | °C | 60 - 90 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 [UL recognition] | UL 94 | 0.75 mm | Class | V-0 |
| Burning behavior UL 94 [UL recognition] | UL 94 | 0.6 mm | Class | V-2 |
| Burning behavior UL 94-5V [UL recognition] | UL 94 | 2.0 mm | Class | 5VB |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.6 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 94 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 83 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 101 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 99 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 3050 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 4.8 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 90 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 87 |
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 10 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | >15 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 45 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 3100 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 3.6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 60 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt volume-flow rate | ISO 1133 | 240 °C/ 5 kg | cm³/10 min | 22 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³ | % | 0.4 - 0.6 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³ | % | 0.4 - 0.6 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 225 |
| Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 29 |
| Surface resistivity | IEC 62631-3-2 | Ohm | 2.0E+13 | |
| Volume resistivity | IEC 62631-3-1 | Ohm*m | 3.0E+14 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 240 | |
| Injection molding - Melt temperature | ISO 294 | °C | 240 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1200 | |
| Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.2 |
| Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.5 |