- Plastics
Bayblend® FR3008 R65
(PC+ABS)-Blend; contains 65% post consumer PC recyclate for natural color; flame retardant; UL recognition 94 V-0 at 1.5 mm
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- CQ mechanical recycled
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 230 - 240 | |
| Barrel Temperatures - Middle | - | °C | 225 - 235 | |
| Barrel Temperatures - Nozzle | - | °C | 255 - 265 | |
| Barrel Temperatures - Rear | - | °C | 220 - 230 | |
| Dry Air Drying Temperature | - | °C | 85 | |
| Dry Air Drying Time | - | h | 4 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 240 - 270 | |
| Moisture Content max. (%) | - | % | <=0.02 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 260 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 (1.5 mm) [UL recognition] | UL 94 | Class | V-0 | |
| Burning behavior UL 94-5V | UL 94 | 2.0 mm | Class | 5VB (Covestro Test) |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 95 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 86 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 103 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 101 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Ball indentation hardness | ISO 2039-1 | New | N/mm² | 136 |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2600 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 95 |
| Izod impact strength | ISO 180/U | -30 °C | kJ/m² | N |
| Izod impact strength | ISO 180/U | 23 °C | kJ/m² | N |
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 30 |
| Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 10 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | >50 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 47 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2500 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 4 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 59 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt volume-flow rate | ISO 1133 | 240 °C/ 5 kg | cm³/10 min | 21 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³/ 240 °C/ MT 80 °C/ 500 bar | % | 0.5-0.6 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³/ 240 °C/ MT 80 °C/ 500 bar | % | 0.5-0.6 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Melt temperature | ISO 294 | °C | 240 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1185 |